Structural analysis of Zn2TiO4 doped with MgO
(Springer, 2009)
The starting mixtures of ZnO, TiO2, and MgO (0, 1.25, and 2.5 wt.%) powders are mechanically activated in a high-energy planetary mill for 15 min and then sintered between 800 and 1100°C for 2 h. The influence of MgO ...
Influence of mechanical activation on synthesis of zinc metatitanate
(Belgrade : International Institute for the Science of Sintering, 2005)
Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...
Influence of MgO addition on the synthesis and electrical properties of sintered zinc-titanate ceramics
(Elsevier, 2009)
Starting mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5 wt.% MgO) powders were mechanically activated for 15 min in a planetary ball mill. The powders obtained were sintered non-isothermally to temperatures between 800 and ...
Structural and magnetic characterization of LiMn1.825Cr0.175O4 spinel obtained by ultrasonic spray pyrolysis
(Materials Research Bulletin, 2007)
Quaternary spinel oxide LiMn1.825Cr0.175O4 Powder was synthesized by using an ultrasonic spray pyrolysis method, without additional annealing. The crystal structure of the as-prepared powder was revealed by X-ray powder ...
Infrared reflection spectroscopy of Zn2SnO4 thin films deposited on silica substrate by radio frequency magnetron sputtering
(Elsevier, 2008)
Single-phase zinc-stannate thin films of different thickness values were prepared by radio frequency magnetron sputtering on a silica substrate. Rietveld analysis of X-ray diffraction data confirmed that the films had an ...
Influence of solvent on the structural and morphological properties of AgI particles prepared using ultrasonic spray pyrolysis
(Materials Chemistry and Physics, 2008)
Silver iodide particles were synthesized in the process of ultrasonic spray pyrolysis using aqueous solutions of thermodynamically stable silver iodide clusters as precursor. The AgI particles were collected in solvents ...
Mechanochemical synthesis and electrical conductivity of nanocrystalline δ-Bi2O3 stabilized by HfO2 and ZrO2
(Belgrade : Serbian Chemical Society, 2009)
A powder mixture of α-Bi2O3 and HfO2, in the molar ratio 2:3, was mechanochemically treated in a planetary ball mill under air, using zirconium oxide vials and balls as the milling medium. After 50 h of milling, the ...