Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Far infrared properties of bulk sintered and thin film Zn2SnO4
(Lausanne : Elsevier Science, 2007)
Room temperature far infrared reflectivity spectra of single phase spinel zinc-stannate thin films, prepared by rf magnetron sputtering on a glass substrate, and bulk sintered samples were measured. The sintered samples ...
Phase evolution in Ce-doped yttrium-aluminum-based particles derived from aerosol
(Oxford : Elsevier Sci, 2007)
The common nitrates precursor solution leading to the Y3Al5O12:Ce3+ (YAG:Ce) composition with 2 at.% of cerium, is ultrasonically atomised and introduced into the tubular flow reactor at 320 degrees C. Having in mind that ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Preparation of nanostructured Zn-Cr-O spinel powders by ultrasonic spray pyrolysis
(Elsevier Sci Ltd, Oxford, 2001)
Ultrasonic spray pyrolysis (1.7 MHz) has been applied for the generation of zinc chromium oxide submicronic (470 nm) particles from the corresponding metal nitrate solution. Heterogeneous gas-liquid/solid chemical reactions ...
Monitoring of transformations in bentonite after NaOH-TMA treatment
(Oxford : Elsevier Sci, 2007)
Semi-quantitative methods of X-ray diffraction and FTIR-spectroscopy, accompanied by electron microscopy, X-ray microanalysis and others were used to monitor structural-phase reorganizations occurring in a smectite-gypsum ...
Microstructural evolution and electric properties of mechanically activated BaTiO3 ceramics
(Oxford : Elsevier Sci Ltd, 2007)
Ceramic materials with a perovskite related structures such as non-doped and doped barium titanate ceramics are attracting much interest for their application as capacitor dielectrics, resistors, thermal sensors, etc. Since ...
Synthesis of BaTiO3 from a mechanically activated BaCO 3-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Far infrared properties of sintered NiO
(Elsevier, 2007)
Far infrared reflection spectra of NiO polycrystals sintered at 1100 °C for various times (30–240 min) were measured at room temperature using a FTIR Spectrometer—Brucker 113V. The measured spectra depended on the sintering ...
Far infrared reflectance of sintered nickel manganite samples for negative temperature coefficient thermistors
(Pergamon-Elsevier Science Ltd, Oxford, 2007)
Single phase complex spinel (Mn, Ni, Co, Fe)(3)O-4 samples were sintered at 1050, 1200 and 1300 degrees C for 30 min and at 1200 degrees C for 120 min. Morphological changes of the obtained samples with the siDtering ...