Densification rate and phase structure changes during sintering of zinc titanate ceramics
(Elsevier, 2009)
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Sintering was performed in a dilatometer in two regimes: the first to 900 °C (heating rates 5, 10 and 15 °C/min) and the ...
Modeling boron separation from water by activated carbon, impregnated and unimpregnated
(Roma : Società chimica italiana, 2000)
The sorption of boron from boric acid water solution by impregnated activated carbon has been studied Barium, calcium, mannitol, tartaric acid and citric acid were used as chemical active materials. All processes were ...
Influence of MgO addition on the synthesis and electrical properties of sintered zinc-titanate ceramics
(Elsevier, 2009)
Starting mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5 wt.% MgO) powders were mechanically activated for 15 min in a planetary ball mill. The powders obtained were sintered non-isothermally to temperatures between 800 and ...
Far infrared reflectance of sintered Zn2TiO4
(Springer Science+Business Media, 2008)
Zinc-titanate ceramics were obtained by initial mechanical activation in a high-energy planetary mill for 15 min followed by sintering at temperatures 900-1100°C for 2 h. Room temperature far infrared reflectivity spectra ...
Synthesis and characterization of zinc titanate nano-crystal powders obtained by mechanical activation
(Belgrade : International Institute for the Science of Sintering, 2005)
Development of dielectric materials for microwave frequencies is increasing with rapid progress in mobile and satellite communications systems, where zinc titanates have found application due to their semi-conducting and ...
Surface analysis of bismuth titanate by Auger and X-ray photoelectron spectroscopy
(Elsevier, 2009)
The Auger and XPS technique has been used for investigation in the surface of bismuth titanate (Bi4Ti3O12) (BIT) ceramics obtained by reactive sintering from Bi2O3 and TiO2 oxides. All peaks characteristic for bismuth, ...
Investigation of sintering kinetics of NiO using photo acoustic spectroscopy
(Belgrade : International Institute for the Science of Sintering, 2004)
Sintering kinetics of NiO was investigated using photo acoustic spectroscopy This method was used to follow the change of phase and amplitude of the photo acoustic signal of nickel-oxide samples sintered at 1373 K for ...
Evaluation of hot-pressed hydroxyapatite/poly-L-lactide composite biomaterial characteristics
(Journal of Biomedical Materials Research. Part B: Applied Biomaterials, 2004)
Hydroxyapatite/poly-L-lactide (HAp/PLLA) is a ceramic/polymer composite, whose application as a resorbable biomaterial for the substitution and repair of hard bone tissue is widely promising in orthopedic, oral, maxillofacial, ...
Preparation and properties of BaTi1-xSnxO3 multilayered ceramics
(Journal of the European Ceramic Society, 2007)
BaTi1-xSnxO3 (BTS) powders, with x ranging from 0 to 0.15, were synthesized by solid-state reaction technique. The powders were pressed and sintered at 1370 degrees C. Obtained BTS ceramics were investigated by X-ray ...
Far infrared properties of sintered PbTe doped with boron
(Belgrade : International Institute for the Science of Sintering, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fitted using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm-1 and 285 ...