Influence of mechanical activation on MgO-TiO2 system
(Belgrade : Institute of Technical Sciences of SASA, 2008)
In this paper the influence of mechanical activation on MgO-TiO2 system has been investigated. Mixtures of MgO-TiO2 were mechanically activated using high-energy planetary ball mill during 0, 5, 10, 20, 40, 80 and 120 ...
Influence of mechanical activation on BaO-ZnO-TiO2 system
(Belgrade : Institute of Technical Sciences of SASA, 2008)
The influence of mechanical activation on BaO-ZnO-TiO2 sistem was observed. Mixtures of BaO-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 0,5, 10, 20, 40 and 80 minutes. XRD analyses ...
Far infrared reflectance of sintered Zn2TiO4
(Springer Science+Business Media, 2008)
Zinc-titanate ceramics were obtained by initial mechanical activation in a high-energy planetary mill for 15 min followed by sintering at temperatures 900-1100°C for 2 h. Room temperature far infrared reflectivity spectra ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Synthesis of BaTiO3 from a mechanically activated BaCO 3-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Sintering of mechanically activated Zno-TiO 2 powders
(Springer, 2008)
Zinc oxide and titanium dioxide powders mixed in an equimolar ratio are mechanically activated in a planetary ball mill and sintered under nonisothermal and isothermal conditions. Nonisothermal sintering is studied using ...
Influence of mechanical activation on MgO-TiO2 system
(2008)
Poster presented at the 10th Conference of the Materials Research Society of Serbia - YUCOMAT 2008, Herceg Novi, Montenegro, September 8-12, 2008