Influence of mechanical activation on synthesis of zinc metatitanate
(Belgrade : International Institute for the Science of Sintering, 2005)
Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...
Synthesis and characterization of zinc titanate nano-crystal powders obtained by mechanical activation
(Belgrade : International Institute for the Science of Sintering, 2005)
Development of dielectric materials for microwave frequencies is increasing with rapid progress in mobile and satellite communications systems, where zinc titanates have found application due to their semi-conducting and ...
Reaction sintering of the 2ZnO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2007)
Sintering kinetics of the mechanically activated ZnO-TiO2 system was studied. Mixtures of ZnO and TiO2 powders were mechanically activated using a high-energy ball mill for different time intervals from 0 to 300 minutes. ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Synthesis of BaTiO3 from a mechanically activated BaCO 3-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Belgrade : International Institute for the Science of Sintering, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
The synthesis - structure relationship in the ZnO-Cr2O3 system
(Belgrade : International Institute for the Science of Sintering, 2004)
In this work the development of the spinel phase in the ZnO-Cr2O3 system was discussed from the viewpoint of the synthesis-structure relationship. The nanostructure evolution in particles obtained either via solution-based ...