Uticaj mehaničke aktivacije na sintezu cink-metatitanata
(Čačak : University of Kragujevac, Faculty of Technical Sciences, Čačak, 2005)
U ovom radu analiziran je uticaj mehaničke aktivacije na sintezu cink-meta titanata (ZnTiO3). Polazeći od toga da mehanička aktivacija utiče na strukturu praha, menjajući je za naknadnu sintezu procesom sinterovanja, mi ...
Structural analysis of Zn2TiO4 doped with MgO
(Springer, 2009)
The starting mixtures of ZnO, TiO2, and MgO (0, 1.25, and 2.5 wt.%) powders are mechanically activated in a high-energy planetary mill for 15 min and then sintered between 800 and 1100°C for 2 h. The influence of MgO ...
Reduction of the specific surface area of porous ZnO during sintering
(Čačak : Technical Faculty, 2007)
In this paper reduction of the specifice surface area of porous ZnO during sintering was analyzed. ZnO was sintered at temperatures from 673K to 1173K. Reduction of the specific surface area was observed as a function of ...
Analiza osetljivosti debeloslojnih NTC termistora na promene temperature i protoka vazduha
(Čačak : University of Kragujevac, Faculty of Technical Sciences, 2006)
NTC termistori na bazi Mn, Ni, Co i Fe oksida za potrebe debeloslojnih senzora pripadaju oblasti istraživačkog i primenjenog rada sa ciljem realizacije senzora prilagođenih po obliku, prenosu toplote i brzini odziva fizičkim ...
The master sintering curves for BaTi0.975Sn0.025O3/BaTi0.85S n0.15O3 functionally graded materials
(Elsevier, 2009)
The most important aim in the design and processing of functionally graded materials (FGMs) is to produce devices free from any deformation. Smart choices of different combination of graded layers, as well as the heating ...
Influence of mechanical activation on structural and electrical properties of sintered MgTiO3 ceramics
(Belgrade : International Institute for the Science of Sintering, 2009)
The aim of this work was to analyze the influence of mechanical activation on the MgCO3-TiO2 system. Mixtures of MgCO3-TiO2 were mechanically activated for 15, 30, 60 and 120 minutes in a planetary ball mill and after that ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Belgrade : International Institute for the Science of Sintering, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Investigation of sintering kinetics of ZnO by observing reduction of the specific surface area
(Belgrade : International Institute for the Science of Sintering, 2007)
Reduction of the specific surface area of porous ZnO during the sintering process was studied. ZnO powder was sintered at temperatures from 673 K to 1173 K. The decrease in the specific surface area was observed as a ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Belgrade : International Institute for the Science of Sintering, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
High temperature sintering kinetics of a-Al2o3 powder
(Belgrade : International Institute for the Science of Sintering, 2003)
The sintering kinetics of a-Al2O3 powder is investigated in this paper Commercial a-Al2O3 powdered compacts were sintered close to 95 % of the theoretical density. The characteristic parameters of sintering kinetics were ...