Dielectric characteristics of polymer nanocomposites based on PVDF and mechanically activated ZnO powder
(Belgrade : Serbian Ceramic Society, 2021)
ZnO powder was mechanically activated for 10 and 30 minutes in a high energy planetary ball mill, and mixed with 2 wt% PVDF solution to obtain nanocomposite films (50 μm) by casting. ZnO powder activated for 10 and 30 ...
The Influence of Synthesis Parameters and Heat Effect on Magnetic Properties of Powder System FexOy - BaTiO3
(Belgrade : Serbian Ceramic Society, 2015)
Powder mixture of 60 mass % of iron (Fe) and 40 mass % of barium titanate (BaTiO3) has been activated in planetary mill for 100, 120, 150, 180, 210 and 240 min in the air. During the activation the iron powder transits ...
Dilatometric Analysis of Mechanically Activated SrTiO3 Powder
(Belgrade : Serbian Ceramic Society, 2013)
Strontium-titanate powder was mechanically activated in a planetary ball mill for 0, 5, 10, 30, 60, 90 and 120 minutes. Non-isothermal sintering of non-activated and activated SrTiO3 powder samples in the temperature ...
The influence of mechanical activation on structural evolution of nanocrystalline SrTiO3 powders
(Elsevier, 2017)
Structural changes caused by mechanical activation of SrTiO3 powders were investigated using a variety of methods. Average crystallite size continuously decreased with increased activation time to around 20 nm after 120 ...
Influence of mechanical activation on synthesis of zinc metatitanate
(Belgrade : International Institute for the Science of Sintering, 2005)
Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...
Influence of synthesis parameters and thermal treatment on functional properties of Fe3O4-BaTiO3 multiferroics obtained by mechanical activation
(Belgrade : Serbian Ceramic Society, 2017)
Mechanical activation of a mixture of polycrystalline powders Fe3O4 (50% wt.) and BaTiO3 (50% wt.) was performed in a planetary ball-mill, with different milling times (3 h, 6 h and 12 h). Average crystallite size determined ...
Structural characterization of mechanically activated MgO-TiO2 system
(Belgrade : Materials Research Society of Serbia, 2011)
Mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for time interval from 0 to 120 minutes. On thus obtained powders, structural investigations have been performed. N2 adsorption method was ...
Influence of mechanical activation on BaO-ZnO-TiO2 system
(Belgrade : Institute of Technical Sciences of SASA, 2008)
The influence of mechanical activation on BaO-ZnO-TiO2 sistem was observed. Mixtures of BaO-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 0,5, 10, 20, 40 and 80 minutes. XRD analyses ...
Synthesis and characterization of zinc titanate nano-crystal powders obtained by mechanical activation
(Belgrade : International Institute for the Science of Sintering, 2005)
Development of dielectric materials for microwave frequencies is increasing with rapid progress in mobile and satellite communications systems, where zinc titanates have found application due to their semi-conducting and ...
Synthesis of BaFe12O19-BaTiO3 multiferroics by mechanical activation
(Belgrade : Serbian Ceramic Society, 2017)
A mixture of polycrystalline powders of Fe (70 % wt.) and BaTiO3 (30 % wt.) was ball-milled in a planetary mill under air atmosphere, for different time intervals: 60, 120, 180, 240, 300 and 360 min. During the mechanical ...