Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Belgrade : International Institute for the Science of Sintering, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Investigation of sintering kinetics of ZnO by observing reduction of the specific surface area
(Belgrade : International Institute for the Science of Sintering, 2007)
Reduction of the specific surface area of porous ZnO during the sintering process was studied. ZnO powder was sintered at temperatures from 673 K to 1173 K. The decrease in the specific surface area was observed as a ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Belgrade : International Institute for the Science of Sintering, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Preparation and properties of BaTi1-xSnxO3 multilayered ceramics
(Journal of the European Ceramic Society, 2007)
BaTi1-xSnxO3 (BTS) powders, with x ranging from 0 to 0.15, were synthesized by solid-state reaction technique. The powders were pressed and sintered at 1370 degrees C. Obtained BTS ceramics were investigated by X-ray ...
Far infrared properties of sintered PbTe doped with boron
(Belgrade : International Institute for the Science of Sintering, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fitted using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm-1 and 285 ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Microstructural evolution and electric properties of mechanically activated BaTiO3 ceramics
(Oxford : Elsevier Sci Ltd, 2007)
Ceramic materials with a perovskite related structures such as non-doped and doped barium titanate ceramics are attracting much interest for their application as capacitor dielectrics, resistors, thermal sensors, etc. Since ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Belgrade : International Institute for the Science of Sintering, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Influence of mechanical activation on synthesis and properties of the MgO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2007)
Materials applied in electronics such as multilayer capacitors are an important field of ceramic materials. Magnesium titanate based dielectric materials are used for producing type-I capacitors. A common way of obtaining ...
Ispitivanje sinterovane cink-kalaj-oksidne keramike fotoakustičnom spektroskopijom
(Beograd : Savez hemijskih inženjera, 2007)
Prahovi ZnO i SnO2 pomešani u molamom odnosu 2:1 mehanički su aktivi- rani u planetamim mlinu sa kuglama u intervalu od 10 do 160 minuta. Do- bijene smeše presovane su i izotermski sinterovane na 1300 °C, dva sata. Uzorci ...