@misc{
author = "Vujančević, Jelena and Andričević, Pavao and Bjelajac, Anđelika and Đokić, Veljko and Popović, Maja and Rakočević, Zlatko and Horváth, Endre and Kollár, Márton and Náfrádi, Bálint and Schiller, Andreas and Domanski, Konrad and Forró, Laszlo and Pavlović, Vera P. and Janaćković, Đorđe",
year = "2019",
abstract = "Table S1. Reported methods for nitrogen doping of anodized TiO2 nanotube arrays; Figure S1. SEM images and statistical distributions of outer diameters obtained by analyzing SEM micrographs of 100 nanotubes; Table S2. Average morphology parameters for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S3. Average crystals size for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S2. Deconvoluted XPS spectra of N 1s core level of Ti foil (black line-experimental, grey line-background, magenta line-envelope); Table S4. Peak positions and atomic percentages of N1s core levels for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S5. Positions and atomic percentages of Ti 2p3/2 and O1s core peaks for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S3. The time evolution of the current during the preconditioning of the TiO2/perovskite sample at a bias voltage of 100 V for 75 sec. Dashed line is the logarithmic fit of the base line of the current time evolution; Figure S4. Ideality factor for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples",
journal = "Ceramics International",
title = "Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045",
url = "https://hdl.handle.net/21.15107/rcub_dais_5969"
}