Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045
Аутори
Vujančević, JelenaAndričević, Pavao
Bjelajac, Anđelika
Đokić, Veljko
Popović, Maja
Rakočević, Zlatko
Horváth, Endre
Kollár, Márton
Náfrádi, Bálint
Schiller, Andreas
Domanski, Konrad
Forró, Laszlo
Pavlović, Vera P.
Janaćković, Đorđe
Скуп података (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Table S1. Reported methods for nitrogen doping of anodized TiO2 nanotube arrays; Figure S1. SEM images and statistical distributions of outer diameters obtained by analyzing SEM micrographs of 100 nanotubes; Table S2. Average morphology parameters for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S3. Average crystals size for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S2. Deconvoluted XPS spectra of N 1s core level of Ti foil (black line-experimental, grey line-background, magenta line-envelope); Table S4. Peak positions and atomic percentages of N1s core levels for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S5. Positions and atomic percentages of Ti 2p3/2 and O1s core peaks for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S3. The time evolution of the current during the preconditioning of the TiO2/perovskite sample at a bias voltage of 100 V for 75 sec. Dashed line is the logarithmic fit of the base line of the curre...nt time evolution; Figure S4. Ideality factor for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples
Кључне речи:
optical properties / annealing in NH 3 / methylammonium lead triiodide photodetectors / photocurrent / titanium dioxide nanotubesИзвор:
Ceramics International, 2019Финансирање / пројекти:
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-172057)
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-45019)
- Swiss National Science Foundation (No. 160169)
- ERC advanced grant “PICOPROP” (Grant No. 670918)
Напомена:
- Related to: https://hdl.handle.net/21.15107/rcub_dais_5765
- Supplementary material for: https://doi.org/10.1016/j.ceramint.2019.02.045
Повезане информације:
- Повезани садржај
https://hdl.handle.net/21.15107/rcub_dais_5765 - Повезани садржај
https://hdl.handle.net/21.15107/rcub_dais_5084 - Повезани садржај
http://dx.doi.org/10.1016/j.ceramint.2019.02.045
Институција/група
Институт техничких наука САНУ / Institute of Technical Sciences of SASATY - DATA AU - Vujančević, Jelena AU - Andričević, Pavao AU - Bjelajac, Anđelika AU - Đokić, Veljko AU - Popović, Maja AU - Rakočević, Zlatko AU - Horváth, Endre AU - Kollár, Márton AU - Náfrádi, Bálint AU - Schiller, Andreas AU - Domanski, Konrad AU - Forró, Laszlo AU - Pavlović, Vera P. AU - Janaćković, Đorđe PY - 2019 UR - https://dais.sanu.ac.rs/123456789/5969 AB - Table S1. Reported methods for nitrogen doping of anodized TiO2 nanotube arrays; Figure S1. SEM images and statistical distributions of outer diameters obtained by analyzing SEM micrographs of 100 nanotubes; Table S2. Average morphology parameters for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S3. Average crystals size for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S2. Deconvoluted XPS spectra of N 1s core level of Ti foil (black line-experimental, grey line-background, magenta line-envelope); Table S4. Peak positions and atomic percentages of N1s core levels for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S5. Positions and atomic percentages of Ti 2p3/2 and O1s core peaks for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S3. The time evolution of the current during the preconditioning of the TiO2/perovskite sample at a bias voltage of 100 V for 75 sec. Dashed line is the logarithmic fit of the base line of the current time evolution; Figure S4. Ideality factor for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples T2 - Ceramics International T1 - Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045 UR - https://hdl.handle.net/21.15107/rcub_dais_5969 ER -
@misc{ author = "Vujančević, Jelena and Andričević, Pavao and Bjelajac, Anđelika and Đokić, Veljko and Popović, Maja and Rakočević, Zlatko and Horváth, Endre and Kollár, Márton and Náfrádi, Bálint and Schiller, Andreas and Domanski, Konrad and Forró, Laszlo and Pavlović, Vera P. and Janaćković, Đorđe", year = "2019", abstract = "Table S1. Reported methods for nitrogen doping of anodized TiO2 nanotube arrays; Figure S1. SEM images and statistical distributions of outer diameters obtained by analyzing SEM micrographs of 100 nanotubes; Table S2. Average morphology parameters for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S3. Average crystals size for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S2. Deconvoluted XPS spectra of N 1s core level of Ti foil (black line-experimental, grey line-background, magenta line-envelope); Table S4. Peak positions and atomic percentages of N1s core levels for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Table S5. Positions and atomic percentages of Ti 2p3/2 and O1s core peaks for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples; Figure S3. The time evolution of the current during the preconditioning of the TiO2/perovskite sample at a bias voltage of 100 V for 75 sec. Dashed line is the logarithmic fit of the base line of the current time evolution; Figure S4. Ideality factor for TiO2-undoped, TiO2-N30, TiO2-N60 and TiO2-N90 samples", journal = "Ceramics International", title = "Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045", url = "https://hdl.handle.net/21.15107/rcub_dais_5969" }
Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V. P.,& Janaćković, Đ.. (2019). Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045. in Ceramics International. https://hdl.handle.net/21.15107/rcub_dais_5969
Vujančević J, Andričević P, Bjelajac A, Đokić V, Popović M, Rakočević Z, Horváth E, Kollár M, Náfrádi B, Schiller A, Domanski K, Forró L, Pavlović VP, Janaćković Đ. Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045. in Ceramics International. 2019;. https://hdl.handle.net/21.15107/rcub_dais_5969 .
Vujančević, Jelena, Andričević, Pavao, Bjelajac, Anđelika, Đokić, Veljko, Popović, Maja, Rakočević, Zlatko, Horváth, Endre, Kollár, Márton, Náfrádi, Bálint, Schiller, Andreas, Domanski, Konrad, Forró, Laszlo, Pavlović, Vera P., Janaćković, Đorđe, "Supporting information for the article: Vujančević, J., Andričević, P., Bjelajac, A., Đokić, V., Popović, M., Rakočević, Z., Horváth, E., Kollár, M., Náfrádi, B., Schiller, A., Domanski, K., Forró, L., Pavlović, V., Janaćković, Đ., 2019. Dry-pressed anodized titania nanotube/CH3NH3PbI3 single crystal heterojunctions: The beneficial role of N doping. Ceramics International 45, 10013–10020. https://doi.org/10.1016/j.ceramint.2019.02.045" in Ceramics International (2019), https://hdl.handle.net/21.15107/rcub_dais_5969 .