Thermal, morphological and mechanical properties of ethyl vanillin immobilized in polyvinyl alcohol by electrospinning process
Pavlović, Vladimir B.
Ostala autorstvaRotaru, Andrei
MetapodaciPrikaz svih podataka o dokumentu
In this study, polyvinyl alcohol (PVA) nanofibers with ethyl vanillin as active compound were prepared using electrospinning technique. The final products of electrospinning process were in the form of films consist of nanofibers. PVNethyl vanillin nanofibers, having fibers diameters in the range 100-1700 nm, were successfully electrospun from ethanol/water mixture of PVA and ethyl vanillin. The effects of immobilization process on ethyl vanillin thermal properties were investigated by differential scanning calorimetry (DSC). The results of DSC showed significant influence of immobilization process on thermal properties of ethyl vanillin. It was noticed that melting point of immobilized ethyl vanillin was lower (~55°C) compared to free flavor (~77°C). Our results showed that films based on PVNethyl vanillin nanofibers are mechanically stable.
Ključne reči:electrospinning / ethyl vanillin / polyvinyl alcohol / differential scanning calorimetry
Izvor:2nd Central and Eastern European Conference on Thermal Analysis and Calorimetry 27-30 August 2013, Vilnius, Lithuania: Book of Abstracts, 2013, 294-294
- Vilnus : Central and Eastern European Committee for Thermal Analysis and Calorimetry
Projekti:[ Google Scholar ]