Electrical properties of mechanochemically activated cordierite ceramics
(Springer, 2012)
Three-component oxide mixtures were prepared containing MgO, Al 2 O 3 and SiO 2 in a 2 : 2 : 5 ratio with addition of 10% Bi 2 O 3. The mixtures were mechanically activated in a range from 5 to 240 min in a mill with ceramic ...
Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema
(Beograd : Savez inženjera i tehničara Srbije, 2012)
U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i ...
Influence of mechanochemical activation on the sintering of cordierite ceramics in the presence of Bi2O3 as a functional additive
(Elsevier, 2012)
Due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good mechanical properties, cordierite, 2MgO⋅2Al2O3⋅ 5SiO2, is a very attractive high-temperature ...
Surface modification of submicronic TiO2 particles prepared by ultrasonic spray pyrolysis for visible light absorption
(Amsterdam : Springer Netherlands, 2012)
Spherical, submicronic TiO2 assemblage with high specific surface area and controllable phase composition was prepared in the process of ultrasonic spray drying/pyrolysis in a wide temperature range (150–800 °C) by using ...
Electrochemical characteristics of rechargeable polyaniline/lead dioxide cell
(Elsevier, 2012)
Electrochemically synthesized polyaniline (PANI) and lead dioxide have been investigated as electrode materials for PANI/1.1 M H2SO4; 0.5 M (NH4)2SO4/PbO2 rechargeable cell. At constant current charge/discharge of the cell, ...
Synthesis of Cerium-Activated Yttrium Aluminate Based Fine Phosphors by an Aerosol Route
(Hoboken, NJ : John Wiley & Sons, 2012)
Polycrystalline fine powders of yttrium aluminate doped with Ce3+ were synthesised by spray pyrolysis of a polymeric precursor, which was obtained by dissolving the corresponding nitrates in a solution of ethylenediamine ...
Influence of mechanical activation on electrical properties of barium–zinc–titanate ceramics sintered at 1100°C
(Springer US, 2012)
Starting mixtures of BaCO3, ZnO, and TiO2 powders are mechanically activated in a planetary ball mill for various periods of time. The powders obtained are sintered isothermally at 1100°C for 120 min. Non-isothermal sintering ...
Mechanical-chemical synthesis Ba0.77Sr0.23TiO3
(Belgrade : International Institute for the Science of Sintering, 2012)
Barium-Strontium-Titanate Ba0.77Sr0.23TiO3 was prepared from starting materials BaCO3, SrCO3 and TiO2 through solid-state reactions. Mixtures of these oxides are mechanically activated in a high-energy planetary ball mill ...