Mixtures of MgO-TiO2 were mechanically activated using high-energy planetary ball mill during 5, 10, 20, 40, 80 and 120 minutes. Sintering process was preformed in air at 1100o-1400oC for 2h. The decrease in powder’s ...

Barium hexaferrite ceramics were prepared using mechanically activated mixtures of iron and barium titanate. The 60:40 mass% Fe:BaTiO3 powder mixtures were mechanically activated for different times (100–240 min) and ...

Cordierite (MAS) is difficult to sinter because of the very narrow sintering temperature range (1300-1400ºC). Because a low temperature process is desirable, it is necessary to find functional ads which can allow easier ...

Ferroelectric barium strontium titanate (Ba0.77Sr0.23TiO3), BST, was prepared by solid-state reactions using as the starting compounds powder of barium carbonate (BaCO3), strontium carbonate (SrCO3) and titanium dioxide ...

In this article, the advantages of combined sintering in comparison with the conventional one, of mechanically activated magnesium titanate ceramic were investigated. The stoichiometric mixtures of MgO and TiO2 were ...

Mechanical activation is commonly used as a pre-sintering process in order to enhance the reactivity of materials, reduce the particle size, increase diffusion rates, accelerate the reaction, and lower the sintering ...