Now showing items 1-2 of 2
The effect of Hot Isostatic Pressing on the MT sample densities
(Belgrade : Serbian Ceramic Society, 2015)
Mechanically activated powders (0, 10, 40, 80 and 160 minutes) were formed by isostatic pressure 300 MPa to cylindrical green bodies (φ 12 mm). First set of samples was sintered at 1300°C for 30 min in air (heating rate ...
Reaction kinetics of mechanically activated cordierite based ceramics studied via DTA
(Ljubljana : Central and Eastern European Committee for Thermal Analysis and Calorimetry, 2015)
Cordierite, 2MgO•2Ah03•5Si02 (MAS), is a very attractive high-temperature ceramic material. In order to accelerate the process of sintering, 5.00 mass% Mo03 was added to the starting mixtures. The mechanical activation of ...