Microstructural and electrical properties of cordierite-based ceramics obtained after two-step sintering technique
(Science of Sintering, 2016)
Cordierite-based ceramic materials are attracting much interest for their various applications in industry, for manufacturing multilayer circuit boards, catalytic converters, filters, thermal insulation, kiln furniture, ...
Influence of prolonged sintering time on density and electrical properties of isothermally sintered cordierite-based ceramics
(Belgrade : International Institute for the Science of Sintering, 2013)
Mechanical activation is a commonly used and relatively fast and inexpensive procedure for sample preparation before the sintering process. Cordierite, a stoichiometric mixture of three different oxides (2MgO⋅2Al2O3⋅5SiO2) ...
Uticaj mehaničke energije na komponente MgO-Al2O3-SiO2-TiO2 sistema
(Beograd : Savez inženjera i tehničara Srbije, 2012)
U ovom radu je ispitivan uticaj mehaničke energije na strukturu i promene u mikrostrukturi sistema MgO-Al2O3-SiO2-TiO2. Utvrđeno je da mehanička energija pospešuje homogenizaciju polaznih komponenti, utiče na veličinu i ...
The influence of compaction pressure on the density and electrical properties of cordierite-based ceramics
(Belgrade : International Institute for the Science of Sintering, 2015)
Due to its characteristics, cordierite, 2MgO·2Al2O3·5SiO2, is a high-temperature ceramic material of a great scientific interest. Mechanical activation of the starting mixtures containing 5.00 mass% TiO2 was performed in ...
Uticaj mehaničke aktivacije na sistem MgO-Al2O3-SiO2 u prisustvu aditiva TeO2 / Influence of mechanical activation on MgO-Al2O3-SiO2 system in the presence of TeO2 additive
(Savez inženjera i tehničara Srbije, Beograd, 2016)
Ova istraživanja posvećena su uticaju mehaničke aktivacije na strukturu kordijeritne smeše 2MgO+2Al2O3+5SiO2. Praćena su i testirana dva paralelna sistema, jedan bez, i drugi u prisustvu 5 masenih % TeO2 kao aditiva. ...
Uticaj mehaničke aktivacije na sistem MgO-Al2O3-SiO2 u prisustvu aditiva TeO2 / Influence of mechanical activation on MgO-Al2O3-SiO2 system in the presence of TeO2 additive
(Beograd : Savez inženjera i tehničara Srbije, 2016)
Ova istraživanja posvećena su uticaju mehaničke aktivacije na strukturu kordijeritne smeše 2MgO+2Al2O3+5SiO2. Praćena su i testirana dva paralelna sistema, jedan bez, i drugi u prisustvu 5 masenih % TeO2 kao aditiva. ...