Reduction of the specific surface area of porous ZnO during sintering
(Čačak : Technical Faculty, 2007)
In this paper reduction of the specifice surface area of porous ZnO during sintering was analyzed. ZnO was sintered at temperatures from 673K to 1173K. Reduction of the specific surface area was observed as a function of ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Belgrade : International Institute for the Science of Sintering, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Investigation of sintering kinetics of ZnO by observing reduction of the specific surface area
(Belgrade : International Institute for the Science of Sintering, 2007)
Reduction of the specific surface area of porous ZnO during the sintering process was studied. ZnO powder was sintered at temperatures from 673 K to 1173 K. The decrease in the specific surface area was observed as a ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Belgrade : International Institute for the Science of Sintering, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Uticaj aditiva na sinterovanje sistema ZnO-TiO2 saglasno trijadi sinteza-struktura-svojstva
(Belgrade : University of Belgrade, Faculty of Physical Chemistry, 2007)
U okviru ove doktorske disertacije detaljno i sistematski je proučen uticaj aditiva magnezijum oksida na sintezu i sinterovanje sistema ZnO-TiO2. Smeša prahova ZnO, TiO2, MgO (0, 1,25 i 2,50 masenih % MgO), mehanički je ...
Preparation and properties of BaTi1-xSnxO3 multilayered ceramics
(Journal of the European Ceramic Society, 2007)
BaTi1-xSnxO3 (BTS) powders, with x ranging from 0 to 0.15, were synthesized by solid-state reaction technique. The powders were pressed and sintered at 1370 degrees C. Obtained BTS ceramics were investigated by X-ray ...
Far infrared properties of sintered PbTe doped with boron
(Belgrade : International Institute for the Science of Sintering, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fitted using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm-1 and 285 ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Microstructural evolution and electric properties of mechanically activated BaTiO3 ceramics
(Oxford : Elsevier Sci Ltd, 2007)
Ceramic materials with a perovskite related structures such as non-doped and doped barium titanate ceramics are attracting much interest for their application as capacitor dielectrics, resistors, thermal sensors, etc. Since ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Belgrade : International Institute for the Science of Sintering, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...