Molecular design of nanoparticles and functional materials by sintering
(Beograd : Tehnološko-metalurški fakultet Univerziteta u Beogradu, 2012)
Nanosized powders present an excellent starting point for the formation of nonporous materials during the sintering process. Narrow particle size distributions and sufficiently small sizes of the precursor powders typically ...
Pseudobrookite TiFe2O5 nanostructured thick films
(Belgrade : Institute of Technical Sciences of SASA, 2015)
TiO2 (anatase) and Fe2O3 (hematite) nanopowders were mixed in the weight ratio 1:1.5 and 1:2 and homogenized in a planetary ball mill for an hour. After that pastes were prepared of the two powder mixtures, organic vehicle ...
Reduction of the specific surface area of porous ZnO during sintering
(Čačak : Technical Faculty, 2007)
In this paper reduction of the specifice surface area of porous ZnO during sintering was analyzed. ZnO was sintered at temperatures from 673K to 1173K. Reduction of the specific surface area was observed as a function of ...
Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors
(IEEE, 2017)
Pseudobrookite thick films were obtained by screen printing paste composed of a 1:1.5 molar ratio mixture of starting nanopowders of hematite and anatase, glass frit and organic binder. The films were deposited on alumina ...
Sintering of Zinc-Titanate
(Atlantis Press, 2016)
Sintering kinetics of the mechanically activated ZnO-TiO2 system was studied. Mixtures of ZnO and TiO2 powders were mechanically activated using a high-energy ball mill for different time intervals from 0 to 300 min. Formal ...
Synthesis and dielectric properties of calcium copper titanate (CCTO) based ceramics
(Belgrade : Institute of Technical Sciences of SASA, 2010)
The perovskite CaCu3Ti4O12 (CCTO) powders with various oxide phase impurities were synthesized via citric gel combustion method. Influence of citric acid amount used for gel preparation was examined in order to lower CCTO ...
Influence of different pore-forming agents on wollastonite microstructures
(Belgrade : Serbian Ceramic Society, 2016)
In this study, highly porous macro- and micro-cellular wollastonite-based ceramics was synthesized. Ceramic precursor, methylhydrocyclosiloxane, together with micro-sized CaCO3, was used as starting material. After 20 min ...
Effects of ball-milling on properties of sintered alumina doped with Mn2O3
(Belgrade : Serbian Ceramic Society, 2018)
Recently, with the huge use of smart gadgets, developing of smart jewelry represents a very interesting segment in material science, as well as in electronic science. Alumina is widely used ceramic in many industrial fields ...
The Influence of Sintering Parameters and Subsequent Thermal Treatment on U-I Characteristics and Degradation of ZnO Varistors
(New York; London : Plenum Press, 1987)
The fabrication of varistor ceramics, characterized by stable electrical properties, was considered on the basis of sintering parameters and subsequent thermal treatment. The process of accelerated degradation of electrical ...
Adsorption capacity of wollastonite based adsorbents with porous structure controlled with different progeny agents
(Belgrade : Serbian Ceramic Society, 2016)
Porous wollastonite (WL) based adsorbents were fabricated by a pressureless sintering process by using low molecular weight poly(methyl methacrylate) (PMMA), nanocellulose (NC) and yeast as the pore forming agents. WL based ...