Mechanical activation as sintering pre-treatment of talc for steatite ceramics
(Belgrade : Interenational Institute for the Science of Sintering, 2014)
The effect of vibratory mill induced mechanical activation on the change of the particle size, crystallinity and the phase transformations of the minerals present in the activated material, was studied with the purpose of ...
Influence of mechanical activation on synthesis and properties of the MgO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2007)
Materials applied in electronics such as multilayer capacitors are an important field of ceramic materials. Magnesium titanate based dielectric materials are used for producing type-I capacitors. A common way of obtaining ...
Sintering of fly ash based composites with zeolite and bentonite addition for application in construction materials
(International Institute for the Science of Sintering, 2017)
Due to pozzolanic characteristics, fly ash is commonly used as a cement replacement in construction composites. Addition of natural clays with sorption ability (i.e. zeolite and bentonite) in to the fly ash based construction ...
Synthesis of barium-zinc-titanate ceramics
(Belgrade : International Institute for the Science of Sintering, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
High temperature sintering kinetics of a-Al2o3 powder
(Belgrade : International Institute for the Science of Sintering, 2003)
The sintering kinetics of a-Al2O3 powder is investigated in this paper Commercial a-Al2O3 powdered compacts were sintered close to 95 % of the theoretical density. The characteristic parameters of sintering kinetics were ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Sintering of mechanically activated magnesium-titanate and barium-zinc-titanate ceramics
(Belgrade : International Institute for the Science of Sintering, 2011)
In this article the influence of mechanical activation on sintering process of magnesium-titanate and barium-zinc-titanate ceramics has been investigated. Both nonactivated and mixtures treated in planetary ball mill for ...
Influence of mechanical activation on microstructure and crystal structure of sintered MgO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2010)
Mixtures of MgO-TiO2 were mechanically activated using high-energy planetary ball mill during 5, 10, 20, 40, 80 and 120 minutes. Sintering process was preformed in air at 1100o-1400oC for 2h. The decrease in powder’s ...
Physical Properties of Sintered Alumina Doped with Different Oxides
(Belgrade : ETRAN, 2018)
Corundum (α-alumina) is a suitable material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition ...
Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
(Science of Sintering, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...