Uticaj mehaničke aktivacije na sintezu cink-metatitanata
(Čačak : University of Kragujevac, Faculty of Technical Sciences, Čačak, 2005)
U ovom radu analiziran je uticaj mehaničke aktivacije na sintezu cink-meta titanata (ZnTiO3). Polazeći od toga da mehanička aktivacija utiče na strukturu praha, menjajući je za naknadnu sintezu procesom sinterovanja, mi ...
Isothermal sintering of mechanically activated MT ceramics
(Kiev, 2009)
The aim of this work was to analyze influence of mechanical activation on MgO-TiO2 system. Mixtures of MgO-TiO2 were mechanically activated for 0, 5, 10, 20, 40, 80 and 120 minutes in a planetary ball mill and after that ...
Influence of mechanical activation on synthesis of zinc metatitanate
(Belgrade : International Institute for the Science of Sintering, 2005)
Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...
Influence of mechanical activation on MgO-TiO2 system
(Belgrade : Institute of Technical Sciences of SASA, 2008)
In this paper the influence of mechanical activation on MgO-TiO2 system has been investigated. Mixtures of MgO-TiO2 were mechanically activated using high-energy planetary ball mill during 0, 5, 10, 20, 40, 80 and 120 ...
Phase Formation at the Sintering of Sa, Zn, Ti Oxides
(Kiev, 2009)
Complex compounds with oxide phases of Ba, 2n, and 11 are widely used in instrument engineering. It is also important to find such production routes for ceramics, which provide their stable structure and properties. Phase ...
Influence of mechanical activation on BaO-ZnO-TiO2 system
(Belgrade : Institute of Technical Sciences of SASA, 2008)
The influence of mechanical activation on BaO-ZnO-TiO2 sistem was observed. Mixtures of BaO-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 0,5, 10, 20, 40 and 80 minutes. XRD analyses ...
Synthesis and characterization of zinc titanate nano-crystal powders obtained by mechanical activation
(Belgrade : International Institute for the Science of Sintering, 2005)
Development of dielectric materials for microwave frequencies is increasing with rapid progress in mobile and satellite communications systems, where zinc titanates have found application due to their semi-conducting and ...
Reaction sintering of the 2ZnO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2007)
Sintering kinetics of the mechanically activated ZnO-TiO2 system was studied. Mixtures of ZnO and TiO2 powders were mechanically activated using a high-energy ball mill for different time intervals from 0 to 300 minutes. ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Synthesis of BaTiO3 from a mechanically activated BaCO 3-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...