Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Belgrade : International Institute for the Science of Sintering, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Investigation of sintering kinetics of ZnO by observing reduction of the specific surface area
(Belgrade : International Institute for the Science of Sintering, 2007)
Reduction of the specific surface area of porous ZnO during the sintering process was studied. ZnO powder was sintered at temperatures from 673 K to 1173 K. The decrease in the specific surface area was observed as a ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Belgrade : International Institute for the Science of Sintering, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Far infrared properties of sintered PbTe doped with boron
(Belgrade : International Institute for the Science of Sintering, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fitted using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm-1 and 285 ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Belgrade : International Institute for the Science of Sintering, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Influence of mechanical activation on synthesis and properties of the MgO-TiO2 system
(Belgrade : International Institute for the Science of Sintering, 2007)
Materials applied in electronics such as multilayer capacitors are an important field of ceramic materials. Magnesium titanate based dielectric materials are used for producing type-I capacitors. A common way of obtaining ...