The aim of this study is to explore the influence of the processing route on the structural and physical properties of bulk MgTiO3 ceramics. Commercially available MgO and TiO2 powders were mechanically activated in a ...

Magnesium aluminate, MgAl2O4 and other alumina-based spinels are ceramics with high hardness, high melting point and mechanical strenght. Spinels can also be used as dielectrics in microwave applications. The goal of this ...

The aim of this work was an investigation of structural and electrical properties of sintered zinc-titanate ceramics obtained by mechanical activation. Mixtures of ZnO and TiO2 were mechanically activated in a planetary ...

The effect of the application of pelletized fly ash based aggregates obtained through different processing techniques on the behavior of lightweight concretes was analyzed. Experimental program implied production of four ...

Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Sintering was performed in a dilatometer in two regimes: the first to 900 °C (heating rates 5, 10 and 15 °C/min) and the ...

The mechanical activation can help reduce production costs and modify cordierite-based materials. In this study, the structure and electrical properties of the mechanically activated MgO-Al2O3-SiO2 system have been analyzed. ...

Nanostructured calcium phosphate functionally graded materials (FGMs) with simultaneous gradients of density, phase composition, and mechanical properties were fabricated by consecutive uniaxial pressing of stoichiometric ...

Starting nanopowders of TiO2 (anatase 99.7%) and α-Fe2O3 (hematite) were mixed in the weight ratios 60:40 and 40:60. Green samples were sintered in the temperature range 750–1250 °C in air. Structural, morphological and ...

Dy/Mn doped BaTiO3 with different Dy2O3 contents, ranging from 0.1 to 5.0 at% Dy, were investigated regarding their microstructural and dielectric characteristics. The content of 0.05 at% Mn was constant in all the ...

Steatite, as ceramic with composition predominantly resting on magnesium silicate, was produced from economic resources – talc, aluminosilicate clays, and either BaCO3 or feldspar as flux. Titanium dioxide was a doping ...