In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...

The influence of mechanical activation on BaO-ZnO-TiO2 sistem was observed. Mixtures of BaO-ZnO-TiO2 were mechanically activated using high-energy planetary ball mill during 0,5, 10, 20, 40 and 80 minutes. XRD analyses ...

Zinc-titanate ceramics were obtained by initial mechanical activation in a high-energy planetary mill for 15 min followed by sintering at temperatures 900-1100°C for 2 h. Room temperature far infrared reflectivity spectra ...

In this paper the influence of mechanical activation on MgO-TiO2 system has been investigated. Mixtures of MgO-TiO2 were mechanically activated using high-energy planetary ball mill during 0, 5, 10, 20, 40, 80 and 120 ...

In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...

Poster presented at the 10th Conference of the Materials Research Society of Serbia - YUCOMAT 2008, Herceg Novi, Montenegro, September 8-12, 2008

Zinc oxide and titanium dioxide powders mixed in an equimolar ratio are mechanically activated in a planetary ball mill and sintered under nonisothermal and isothermal conditions. Nonisothermal sintering is studied using ...