Characterisation of dispersive systems using a coherer
(Belgrade : International Institute for the Science of Sintering, 2002)
The possibility of characterization of aluminium powders using a horizontal coherer has been considered. Al powders of known dimension were treated with a high frequency electromagnetic field or with a DC electric field, ...
Correlation between isothermal expansion and functional properties change of the Fe81B13Si4C2 amorphous alloy
(Belgrade : International Institute for the Science of Sintering, 2009)
The structural changes effect on functional properties of ribbon shaped samples of the Fe81B13Si4C2 amorphous alloy during annealing process was investigated in this paper. Differential scanning calorimetry method has shown ...
Influence of mechanical activation on structural and electrical properties of sintered MgTiO3 ceramics
(Belgrade : International Institute for the Science of Sintering, 2009)
The aim of this work was to analyze the influence of mechanical activation on the MgCO3-TiO2 system. Mixtures of MgCO3-TiO2 were mechanically activated for 15, 30, 60 and 120 minutes in a planetary ball mill and after that ...
Influence of mechanical activation on synthesis of zinc metatitanate
(Belgrade : International Institute for the Science of Sintering, 2005)
Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Belgrade : International Institute for the Science of Sintering, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Investigation of sintering kinetics of ZnO by observing reduction of the specific surface area
(Belgrade : International Institute for the Science of Sintering, 2007)
Reduction of the specific surface area of porous ZnO during the sintering process was studied. ZnO powder was sintered at temperatures from 673 K to 1173 K. The decrease in the specific surface area was observed as a ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Belgrade : International Institute for the Science of Sintering, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Photoacoustic properties of single crystal PbTe(Ni)
(Belgrade : International Institute for the Science of Sintering, 2007)
Single crystals of PbTe(Ni) were investigated by the photoacoustic method. They were produced using the Bridgeman method. These crystals have a sodium chloride cubic lattice and could be cleaved paralel to the plane ...
Geometrical and electrical properties of NTC polycrystalline thermistors vs. Changes of sintering parameters
(Belgrade : International Institute for the Science of Sintering, 2006)
NTC thermistor powder was made of a Mn, Ni, Fe and Co oxide mixture calcinated at 1050°C / 60 min. The powder was milled in a ball mill down to an average particle diameter of 0.9 μm. Small disc shaped pills of the powder ...
High temperature sintering kinetics of a-Al2o3 powder
(Belgrade : International Institute for the Science of Sintering, 2003)
The sintering kinetics of a-Al2O3 powder is investigated in this paper Commercial a-Al2O3 powdered compacts were sintered close to 95 % of the theoretical density. The characteristic parameters of sintering kinetics were ...