During the last decade zinc oxide (ZnO) has attracted considerable attention as a promising material for electronic, optoelectronic and spintronic devices. ZnO has a wide bandgap (3.37 eV at room temperature) and relatively ...

Alumina-based compounds have many technological applications and attract great attention even after decades of investigation, due to their good chemical, electrical, and mechanical properties. A mixture of several alumina ...

Single crystalline phase MgAl2O4 is made from the predetermined composition of MgO-Al2O3 powder mixture by using ball-milling. Mixtures of MgO and Al2O3 are treated in planetary ball mill for 30, 60, 90 and 120 minutes, ...

The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...

The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during heating in nitrogen and air atmosphere. Interactions of bulk specimens with gaseous surrounding induce microstructure ...

One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...

The aim of this study was to improve the mechanical properties and to optimize antimicrobial activity of hydroxyapatite (HAP) by simultaneous doping with Mg and Cu ions in order to obtain material that would be able to ...

The aim of this study was to improve the mechanical properties and to optimize antimicrobial activity of hydroxyapatite (HAP) by simultaneous doping with Mg and Cu ions in order to obtain material that would be able to ...

Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...

TiO2 (anatase) and Fe2O3 (hematite) nanopowders were mixed in the weight ratio 1:1.5 and 1:2 and homogenized in a planetary ball mill for an hour. After that pastes were prepared of the two powder mixtures, organic vehicle ...