The possibility of characterization of aluminium powders using a horizontal coherer has been considered. Al powders of known dimension were treated with a high frequency electromagnetic field or with a DC electric field, ...

Single crystals of PbTe(Ni) were investigated by the photoacoustic method. They were produced using the Bridgeman method. These crystals have a sodium chloride cubic lattice and could be cleaved paralel to the plane ...

NTC thermistor powder was made of a Mn, Ni, Fe and Co oxide mixture calcinated at 1050°C / 60 min. The powder was milled in a ball mill down to an average particle diameter of 0.9 μm. Small disc shaped pills of the powder ...

In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...

The sintering kinetics of a-Al2O3 powder is investigated in this paper Commercial a-Al2O3 powdered compacts were sintered close to 95 % of the theoretical density. The characteristic parameters of sintering kinetics were ...

The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...

Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fitted using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm-1 and 285 ...

Sintering kinetics of the mechanically activated ZnO-TiO2 system was studied. Mixtures of ZnO and TiO2 powders were mechanically activated using a high-energy ball mill for different time intervals from 0 to 300 minutes. ...

Investigations of a ZnO-TiO2 binary oxide mixture during mechanical treatment were mainly focused on obtaining orthotitanate Zn2TiO4 with a spinel structure. Due to the specific way of energy transfer during mechanical ...

Hydroxyapatite/poly-L-lactide (HAp/PLL) composite biomaterial can be obtained by different processing methods. Three-dimensional blocks of HAp/PLLA composite biomaterial with mechanical characteristics close to the natural ...