Uticaj mehaničke aktivacije na sintezu cink-metatitanata
(Čačak : University of Kragujevac, Faculty of Technical Sciences, Čačak, 2005)
U ovom radu analiziran je uticaj mehaničke aktivacije na sintezu cink-meta titanata (ZnTiO3). Polazeći od toga da mehanička aktivacija utiče na strukturu praha, menjajući je za naknadnu sintezu procesom sinterovanja, mi ...
Intrinsic resistivity of sintered Nickel Manganite vs. powder activation time and density
(Belgrade : International Institute for the Science of Sintering, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Densification rate and phase structure changes during sintering of zinc titanate ceramics
(Elsevier, 2009)
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Sintering was performed in a dilatometer in two regimes: the first to 900 °C (heating rates 5, 10 and 15 °C/min) and the ...
High temperature sintering kinetics of a-Al2o3 powder
(Belgrade : International Institute for the Science of Sintering, 2003)
The sintering kinetics of a-Al2O3 powder is investigated in this paper Commercial a-Al2O3 powdered compacts were sintered close to 95 % of the theoretical density. The characteristic parameters of sintering kinetics were ...
Influence of MgO addition on the synthesis and electrical properties of sintered zinc-titanate ceramics
(Elsevier, 2009)
Starting mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5 wt.% MgO) powders were mechanically activated for 15 min in a planetary ball mill. The powders obtained were sintered non-isothermally to temperatures between 800 and ...
Structural analysis of Zn2TiO4 doped with MgO
(Springer, 2009)
The starting mixtures of ZnO, TiO2, and MgO (0, 1.25, and 2.5 wt.%) powders are mechanically activated in a high-energy planetary mill for 15 min and then sintered between 800 and 1100°C for 2 h. The influence of MgO ...
Analiza osetljivosti debeloslojnih NTC termistora na promene temperature i protoka vazduha
(Čačak : University of Kragujevac, Faculty of Technical Sciences, 2006)
NTC termistori na bazi Mn, Ni, Co i Fe oksida za potrebe debeloslojnih senzora pripadaju oblasti istraživačkog i primenjenog rada sa ciljem realizacije senzora prilagođenih po obliku, prenosu toplote i brzini odziva fizičkim ...
Reduction of the specific surface area of porous ZnO during sintering
(Čačak : Technical Faculty, 2007)
In this paper reduction of the specifice surface area of porous ZnO during sintering was analyzed. ZnO was sintered at temperatures from 673K to 1173K. Reduction of the specific surface area was observed as a function of ...
The master sintering curves for BaTi0.975Sn0.025O3/BaTi0.85S n0.15O3 functionally graded materials
(Elsevier, 2009)
The most important aim in the design and processing of functionally graded materials (FGMs) is to produce devices free from any deformation. Smart choices of different combination of graded layers, as well as the heating ...
Structural and electrical properties of sintered zinc-titanate ceramics
(Elsevier, 2009)
The aim of this work was an investigation of structural and electrical properties of sintered zinc-titanate ceramics obtained by mechanical activation. Mixtures of ZnO and TiO2 were mechanically activated in a planetary ...