Infrared reflection spectroscopy of Zn2SnO4 thin films deposited on silica substrate by radio frequency magnetron sputtering
(Elsevier, 2008)
Single-phase zinc-stannate thin films of different thickness values were prepared by radio frequency magnetron sputtering on a silica substrate. Rietveld analysis of X-ray diffraction data confirmed that the films had an ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Far infrared properties of bulk sintered and thin film Zn2SnO4
(Lausanne : Elsevier Science, 2007)
Room temperature far infrared reflectivity spectra of single phase spinel zinc-stannate thin films, prepared by rf magnetron sputtering on a glass substrate, and bulk sintered samples were measured. The sintered samples ...
Phase evolution in Ce-doped yttrium-aluminum-based particles derived from aerosol
(Oxford : Elsevier Sci, 2007)
The common nitrates precursor solution leading to the Y3Al5O12:Ce3+ (YAG:Ce) composition with 2 at.% of cerium, is ultrasonically atomised and introduced into the tubular flow reactor at 320 degrees C. Having in mind that ...
Far infrared reflectance of sintered nickel manganite samples for negative temperature coefficient thermistors
(Pergamon-Elsevier Science Ltd, Oxford, 2007)
Single phase complex spinel (Mn, Ni, Co, Fe)(3)O-4 samples were sintered at 1050, 1200 and 1300 degrees C for 30 min and at 1200 degrees C for 120 min. Morphological changes of the obtained samples with the siDtering ...
Uticaj dopiranja niklom na optička, transportna i neka toplotna svojstva olovo-telurida
(Belgrade : University of belgrade, Faculty of Physics, 2005)
Ova teza je nastala kao rezultat ispitivanja optičkih, transportnih i pojedinih toplotnih svojstava legure PbTe(Ni). Korišćena su dva monokristalna uzorka sa različitim sadržajem Ni, prvi-0.29 % Ni i drugi-sa nešto većom ...
Changes of Structural, Optical and Electrical Properties of Nickel-Manganite Ceramics Induced by Additional Mechanical Activation
(2007)
Poster presented at the 10th International Conference and Exhibition of the European Ceramic Society, Berlin, June 17-21, 2007