Materials based on ZnO structure have more frequently application as fillers in polymer ceramics nanocompozites. Performances of these materials depends on fillers morphology, surfaces texture and particles size. According ...

Ferroelectric ceramic barium strontium titanate (Ba0.77Sr0.23TiO3), BST, was prepared by solid-state reactions using starting powders of barium carbonate (BaCO3), strontium carbonate (SrCO3) and titanium dioxide (TiO2-anatase). ...

In this article the influence of ball miling process on structure of MgO-TiO2 system was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 ...

The materials based on BaTiO3 can be controlled using different technological parameters and different additives. We investigate the influence of different temperature levels of sintering (1320°C, 1350°C and 1380°C) on the ...

In this paper, dielectric characterization of porous alumo-silicate ceramics, modified by alloying with magnesium and microalloying with aluminum, was investigated. Microstructure investigations have revealed non-uniform ...

Vibration-based mechanical energy is one of the most accessible energy source in the surroundings. Harvesting this type of energy exhibits a great potential for remote/wireless sensing, charging batteries, and powering ...

The mixed oxide of CaO·ZnO and K2CO3 were prepared by ball milling of CaO and ZnO powders and water, with addition of K2CO3 and afterward by calcination at 700 oC. Influence of different molar ratio of K2CO3 and CaO (x=1, ...

As coal combustion byproduct fly ash represents a risk for environment: direct ash emission from open land-fills causes pollution of air, soil and water. The solution for this severe pollution problem is fly ash reapplication ...

Strontium-titanate powder was mechanically activated in a planetary ball mill for 0, 5, 10, 30, 60, 90 and 120 minutes. Non-isothermal sintering of non-activated and activated SrTiO3 powder samples in the temperature ...

Cordierite, 2MgO⋅2Al2O3⋅5SiO2, is a very attractive high-temperature ceramic material, due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good ...