Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
(Science of Sintering, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Influence of starting powder milling on magnetic properties of Mn-Zn ferrite
(Novi Sad : Faculty of Technology, University of Novi Sad, 2017)
In this paper, the influence of additional sieving and milling of starting industrial Mn-Zn powders on magnetic properties was investigated. The starting powder was milled for 60 minutes, followed by sieving through 325 ...
Synthesis, characterization and in vitro evaluation of divalent ion release from stable NiFe2O4, ZnFe2O4 and core-shell ZnFe2O4@NiFe2O4 nanoparticles
(Elsevier, 2020)
A simple organic-phase synthesis process was used to produce bare NiFe2O4 and ZnFe2O4 and core-shell ZnFe2O4@NiFe2O4 ferrite nanoparticles. X-ray powder diffractograms for all investigated powders show characteristic peaks ...