Ba0.8Sr0.2TiO3 was prepared from the starting materials BaCO3, SrCO3 and TiO2 through solid state reaction. Mixtures of these oxides were mechanically activated using a high-energy ball mill at different time intervals from 0 to 120 minutes. X-ray diffraction was employed in order to determine the crystal structure and gave information about composition of phase variation. It was observed that after 40 minutes early synthesis of Ba0.8Sr0.2TiO3 phase occurred. Particle size distribution along with scanning electron microscopy gave very useful information about powder morphology.
TY - CONF
AU - Kosanović, Darko
AU - Filipović, Suzana
AU - Obradović, Nina
AU - Mitrić, Miodrag
AU - Marković, Smilja
AU - Maričić, Aleksa
AU - Pavlović, Vladimir B.
AU - Ristić, Momčilo M.
PY - 2011
UR - https://dais.sanu.ac.rs/123456789/630
AB - Ba0.8Sr0.2TiO3 was prepared from the starting materials BaCO3, SrCO3 and TiO2 through solid state reaction. Mixtures of these oxides were mechanically activated using a high-energy ball mill at different time intervals from 0 to 120 minutes. X-ray diffraction was employed in order to determine the crystal structure and gave information about composition of phase variation. It was observed that after 40 minutes early synthesis of Ba0.8Sr0.2TiO3 phase occurred. Particle size distribution along with scanning electron microscopy gave very useful information about powder morphology.
PB - Belgrade : Materials Research Society of Serbia
C3 - The Thirteenth Annual Conference YUCOMAT 2011: Programme and the Book of Abstracts
T1 - Mechanochemical synthesis of Ba0.8Sr0.2TiO3
SP - 134
EP - 134
UR - https://hdl.handle.net/21.15107/rcub_dais_630
ER -
@conference{
author = "Kosanović, Darko and Filipović, Suzana and Obradović, Nina and Mitrić, Miodrag and Marković, Smilja and Maričić, Aleksa and Pavlović, Vladimir B. and Ristić, Momčilo M.",
year = "2011",
abstract = "Ba0.8Sr0.2TiO3 was prepared from the starting materials BaCO3, SrCO3 and TiO2 through solid state reaction. Mixtures of these oxides were mechanically activated using a high-energy ball mill at different time intervals from 0 to 120 minutes. X-ray diffraction was employed in order to determine the crystal structure and gave information about composition of phase variation. It was observed that after 40 minutes early synthesis of Ba0.8Sr0.2TiO3 phase occurred. Particle size distribution along with scanning electron microscopy gave very useful information about powder morphology.",
publisher = "Belgrade : Materials Research Society of Serbia",
journal = "The Thirteenth Annual Conference YUCOMAT 2011: Programme and the Book of Abstracts",
title = "Mechanochemical synthesis of Ba0.8Sr0.2TiO3",
pages = "134-134",
url = "https://hdl.handle.net/21.15107/rcub_dais_630"
}
Kosanović, D., Filipović, S., Obradović, N., Mitrić, M., Marković, S., Maričić, A., Pavlović, V. B.,& Ristić, M. M.. (2011). Mechanochemical synthesis of Ba0.8Sr0.2TiO3. in The Thirteenth Annual Conference YUCOMAT 2011: Programme and the Book of Abstracts
Belgrade : Materials Research Society of Serbia., 134-134.
https://hdl.handle.net/21.15107/rcub_dais_630
Kosanović D, Filipović S, Obradović N, Mitrić M, Marković S, Maričić A, Pavlović VB, Ristić MM. Mechanochemical synthesis of Ba0.8Sr0.2TiO3. in The Thirteenth Annual Conference YUCOMAT 2011: Programme and the Book of Abstracts. 2011;:134-134.
https://hdl.handle.net/21.15107/rcub_dais_630 .
Kosanović, Darko, Filipović, Suzana, Obradović, Nina, Mitrić, Miodrag, Marković, Smilja, Maričić, Aleksa, Pavlović, Vladimir B., Ristić, Momčilo M., "Mechanochemical synthesis of Ba0.8Sr0.2TiO3" in The Thirteenth Annual Conference YUCOMAT 2011: Programme and the Book of Abstracts (2011):134-134,
https://hdl.handle.net/21.15107/rcub_dais_630 .