The aim of this work was an investigation of structural and electrical properties of sintered barium-zinc-titanate ceramics. Mixtures of BaCO3, ZnO and TiO2 were mechanically activated in a planetary ball mill up to 80 minutes and sintered isothermally in air for 120 minutes at 1300°C. The phase composition in the BaCO3-ZnO-TiO2 system after milling and sintering was analyzed using the XRD method. The existence of pure barium-zinc-titanate has been registered. Microstructure analyses were performed using SEM. The results of electric resistivity, capacitance and loss tangent of the sintered samples were correlated with the XRD and SEM
results.
TY - CONF
AU - Obradović, Nina
AU - Filipović, Suzana
AU - Pavlović, Vladimir B.
AU - Paunović, Vesna
AU - Mitrić, Miodrag
AU - Ristić, Momčilo M.
PY - 2010
UR - http://dais.sanu.ac.rs/123456789/626
AB - The aim of this work was an investigation of structural and electrical properties of sintered barium-zinc-titanate ceramics. Mixtures of BaCO3, ZnO and TiO2 were mechanically activated in a planetary ball mill up to 80 minutes and sintered isothermally in air for 120 minutes at 1300°C. The phase composition in the BaCO3-ZnO-TiO2 system after milling and sintering was analyzed using the XRD method. The existence of pure barium-zinc-titanate has been registered. Microstructure analyses were performed using SEM. The results of electric resistivity, capacitance and loss tangent of the sintered samples were correlated with the XRD and SEM
results.
PB - Belgrade : Institute of Technical Sciences of SASA
C3 - Programme and The Book of Abstracts / Twelfth Annual Conference YUCOMAT 2010, Herceg Novi, September 6–10, 2010
T1 - Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc
SP - 118
EP - 118
ER -
@conference{
author = "Obradović, Nina and Filipović, Suzana and Pavlović, Vladimir B. and Paunović, Vesna and Mitrić, Miodrag and Ristić, Momčilo M.",
year = "2010",
url = "http://dais.sanu.ac.rs/123456789/626",
abstract = "The aim of this work was an investigation of structural and electrical properties of sintered barium-zinc-titanate ceramics. Mixtures of BaCO3, ZnO and TiO2 were mechanically activated in a planetary ball mill up to 80 minutes and sintered isothermally in air for 120 minutes at 1300°C. The phase composition in the BaCO3-ZnO-TiO2 system after milling and sintering was analyzed using the XRD method. The existence of pure barium-zinc-titanate has been registered. Microstructure analyses were performed using SEM. The results of electric resistivity, capacitance and loss tangent of the sintered samples were correlated with the XRD and SEM
results.",
publisher = "Belgrade : Institute of Technical Sciences of SASA",
journal = "Programme and The Book of Abstracts / Twelfth Annual Conference YUCOMAT 2010, Herceg Novi, September 6–10, 2010",
title = "Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc",
pages = "118-118"
}
Obradović N, Filipović S, Pavlović VB, Paunović V, Mitrić M, Ristić MM. Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc. Programme and The Book of Abstracts / Twelfth Annual Conference YUCOMAT 2010, Herceg Novi, September 6–10, 2010. 2010;:118-118
Obradović, N., Filipović, S., Pavlović, V. B., Paunović, V., Mitrić, M.,& Ristić, M. M. (2010). Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc.
Programme and The Book of Abstracts / Twelfth Annual Conference YUCOMAT 2010, Herceg Novi, September 6–10, 2010Belgrade : Institute of Technical Sciences of SASA., 118-118.
Obradović Nina, Filipović Suzana, Pavlović Vladimir B., Paunović Vesna, Mitrić Miodrag, Ristić Momčilo M., "Structural and electrical properties of barium-zinc-titanate ceramics sintered at 1300ºc" (2010):118-118