A facile route for hydroxyapatite densification with an increased heating rate
Članak u časopisu (Recenzirana verzija)
MetapodaciPrikaz svih podataka o dokumentu
The densification behavior of hydroxyapatite nanorods prepared by chemical precipitation method in open reactor conditions was investigated by application of different heating rates. The non-isothermal processing was performed with 2, 10, and 50 °C/min up to 1200 °C and yielded fully dense ceramics. The implementation of the higher heating rate provided grain size refinement from micrometer level for the slowest ramp, down to 250 nm in the case of processing with 50 °C/min, without any drawbacks regarding final density. The relative amount of retained structural hydroxyl groups in sintered ceramics was gradually increased with the heating rate. Furthermore, the qualitative level of optical translucency was increased with a higher heating rate which can be explained by the beneficial alignment of HAp nanorods during the fast heating rate processing, achieved microstructural refinement, and higher amount of structural hydroxyl groups.
Ključne reči:hydroxyapatite nanorods / chemical precipitation / non-isothermal processing / heating rate
Izvor:Materials Letters, 2017, 207, 12-15
- Molekularno dizajniranje nanočestica kontrolisanih morfoloških i fizičko-hemijskih karakteristika i funkcionalnih materijala na njihovoj osnovi (RS-45004)
- This is the peer-reviewed version of the article: Lukić, M.J., Sezen, M., Veljović, Đ., Mraković, A., 2017. A facile route for hydroxyapatite densification with an increased heating rate. Materials Letters 207, 12–15. https://doi.org/10.1016/j.matlet.2017.07.020