A facile route for hydroxyapatite densification with an increased heating rate
Чланак у часопису (Рецензирана верзија)
МетаподациПриказ свих података о документу
The densification behavior of hydroxyapatite nanorods prepared by chemical precipitation method in open reactor conditions was investigated by application of different heating rates. The non-isothermal processing was performed with 2, 10, and 50 °C/min up to 1200 °C and yielded fully dense ceramics. The implementation of the higher heating rate provided grain size refinement from micrometer level for the slowest ramp, down to 250 nm in the case of processing with 50 °C/min, without any drawbacks regarding final density. The relative amount of retained structural hydroxyl groups in sintered ceramics was gradually increased with the heating rate. Furthermore, the qualitative level of optical translucency was increased with a higher heating rate which can be explained by the beneficial alignment of HAp nanorods during the fast heating rate processing, achieved microstructural refinement, and higher amount of structural hydroxyl groups.
Кључне речи:hydroxyapatite nanorods / chemical precipitation / non-isothermal processing / heating rate
Извор:Materials Letters, 2017, 207, 12-15
- Молекуларно дизајнирање наночестица контролисаних морфолошких и физичко-хемијских карактеристика и функционалних материјала на њиховој основи (RS-45004)
- This is the peer-reviewed version of the article: Lukić, M.J., Sezen, M., Veljović, Đ., Mraković, A., 2017. A facile route for hydroxyapatite densification with an increased heating rate. Materials Letters 207, 12–15. https://doi.org/10.1016/j.matlet.2017.07.020