DAIS - Digital Archive of the Serbian Academy of Sciences and Arts
    • English
    • Српски
    • Српски (Serbia)
  • English 
    • English
    • Serbian (Cyrillic)
    • Serbian (Latin)
  • Login
View Item 
  •   DAIS
  • Институт техничких наука САНУ / Institute of Technical Sciences of SASA
  • ИТН САНУ - Општа колекција / ITS SASA - General collection
  • View Item
  •   DAIS
  • Институт техничких наука САНУ / Institute of Technical Sciences of SASA
  • ИТН САНУ - Општа колекција / ITS SASA - General collection
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.

Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films

Thumbnail
2018
10.1016@j.snb.2018.09.063.pdf (1.707Mb)
Authors
Nikolić, Maria Vesna
Vasiljević, Zorka Ž.
Luković, Miloljub D.
Pavlović, Vera P.
Vujančević, Jelena
Radovanović, Milan
Krstić, Jugoslav
Vlahović, Branislav
Pavlović, Vladimir B.
Article (Accepted Version)
Metadata
Show full item record
Abstract
Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (α-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 °C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range ...42 Hz–1 MHz with humidity was analyzed at room temperature (25 °C) and 50 °C in the relative humidity range 30–90% and 40–90%, respectively. At 42 Hz, and room temperature the impedance reduced ∼28 times, while at 50 °C it reduced ∼147 times in the relative humidity range 40–90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 °C and 2.64% at 50 °C) showing that this is a promising material for application in humidity sensing.

Keywords:
FeTiO / humidity sensors / pseudobrookite / thick films
Source:
Sensors and Actuators B: Chemical, 2018, 277, 654-664
Publisher:
  • Elsevier
Funding / projects:
  • Zero- to Three-Dimensional Nanostructures for Application in Electronics and Renewable Energy Sources: Synthesis, Characterization and Processing (RS-45007)
  • Lithium-ion batteries and fuel cells - research and development (RS-45014)
Note:
  • This is the peer-reviewed version of the article: Nikolic, M.V., Vasiljevic, Z.Z., Lukovic, M.D., Pavlovic, V.P., Vujancevic, J., Radovanovic, M., Krstic, J.B., Vlahovic, B., Pavlovic, V.B., 2018. Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. Sensors and Actuators B: Chemical 277, 654–664. https://doi.org/10.1016/j.snb.2018.09.063

DOI: 10.1016/j.snb.2018.09.063

ISSN: 0925-4005

WoS: 000453066700081

Scopus: 2-s2.0-85053789141
[ Google Scholar ]
34
22
Handle
https://hdl.handle.net/21.15107/rcub_dais_4605
URI
http://www.sciencedirect.com/science/article/pii/S0925400518316836
https://dais.sanu.ac.rs/123456789/4605
Collections
  • ИТН САНУ - Општа колекција / ITS SASA - General collection
Institution/Community
Институт техничких наука САНУ / Institute of Technical Sciences of SASA
TY  - JOUR
AU  - Nikolić, Maria Vesna
AU  - Vasiljević, Zorka Ž.
AU  - Luković, Miloljub D.
AU  - Pavlović, Vera P.
AU  - Vujančević, Jelena
AU  - Radovanović, Milan
AU  - Krstić, Jugoslav
AU  - Vlahović, Branislav
AU  - Pavlović, Vladimir B.
PY  - 2018
UR  - http://www.sciencedirect.com/science/article/pii/S0925400518316836
UR  - https://dais.sanu.ac.rs/123456789/4605
AB  - Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (α-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 °C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz–1 MHz with humidity was analyzed at room temperature (25 °C) and 50 °C in the relative humidity range 30–90% and 40–90%, respectively. At 42 Hz, and room temperature the impedance reduced ∼28 times, while at 50 °C it reduced ∼147 times in the relative humidity range 40–90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 °C and 2.64% at 50 °C) showing that this is a promising material for application in humidity sensing.
PB  - Elsevier
T2  - Sensors and Actuators B: Chemical
T1  - Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films
SP  - 654
EP  - 664
VL  - 277
DO  - 10.1016/j.snb.2018.09.063
UR  - https://hdl.handle.net/21.15107/rcub_dais_4605
ER  - 
@article{
author = "Nikolić, Maria Vesna and Vasiljević, Zorka Ž. and Luković, Miloljub D. and Pavlović, Vera P. and Vujančević, Jelena and Radovanović, Milan and Krstić, Jugoslav and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2018",
abstract = "Pseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (α-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 °C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz–1 MHz with humidity was analyzed at room temperature (25 °C) and 50 °C in the relative humidity range 30–90% and 40–90%, respectively. At 42 Hz, and room temperature the impedance reduced ∼28 times, while at 50 °C it reduced ∼147 times in the relative humidity range 40–90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 °C and 2.64% at 50 °C) showing that this is a promising material for application in humidity sensing.",
publisher = "Elsevier",
journal = "Sensors and Actuators B: Chemical",
title = "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films",
pages = "654-664",
volume = "277",
doi = "10.1016/j.snb.2018.09.063",
url = "https://hdl.handle.net/21.15107/rcub_dais_4605"
}
Nikolić, M. V., Vasiljević, Z. Ž., Luković, M. D., Pavlović, V. P., Vujančević, J., Radovanović, M., Krstić, J., Vlahović, B.,& Pavlović, V. B.. (2018). Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B: Chemical
Elsevier., 277, 654-664.
https://doi.org/10.1016/j.snb.2018.09.063
https://hdl.handle.net/21.15107/rcub_dais_4605
Nikolić MV, Vasiljević ZŽ, Luković MD, Pavlović VP, Vujančević J, Radovanović M, Krstić J, Vlahović B, Pavlović VB. Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films. in Sensors and Actuators B: Chemical. 2018;277:654-664.
doi:10.1016/j.snb.2018.09.063
https://hdl.handle.net/21.15107/rcub_dais_4605 .
Nikolić, Maria Vesna, Vasiljević, Zorka Ž., Luković, Miloljub D., Pavlović, Vera P., Vujančević, Jelena, Radovanović, Milan, Krstić, Jugoslav, Vlahović, Branislav, Pavlović, Vladimir B., "Humidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick films" in Sensors and Actuators B: Chemical, 277 (2018):654-664,
https://doi.org/10.1016/j.snb.2018.09.063 .,
https://hdl.handle.net/21.15107/rcub_dais_4605 .

DSpace software copyright © 2002-2015  DuraSpace
About DAIS - Digital Archive of the Serbian Academy of Sciences and Arts | Send Feedback

CoreTrustSealre3dataOpenAIRERCUB
 

 

All of DSpaceInstitutions/communitiesAuthorsTitlesSubjectsThis institutionAuthorsTitlesSubjects

Statistics

View Usage Statistics

DSpace software copyright © 2002-2015  DuraSpace
About DAIS - Digital Archive of the Serbian Academy of Sciences and Arts | Send Feedback

CoreTrustSealre3dataOpenAIRERCUB