Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors
Samo za registrovane korisnike
2017
Autori
Mišković, GoranNikolić, Maria Vesna
Luković, Miloljub D.
Vasiljević, Zorka Ž.
Nicolics, Johann
Aleksić, Obrad S.
Konferencijski prilog (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Pseudobrookite thick films were obtained by screen printing paste composed of a 1:1.5 molar ratio mixture of starting nanopowders of hematite and anatase, glass frit and organic binder. The films were deposited on alumina substrates with interdigitated electrode geometry. Sintering at 850 °C resulted in the formation of pseudobrookite. X-Ray Diffraction (XRD) analysis showed pseudobrookite with a mixed orthorhombic and monoclinic structure and a small amount of excess rutile. Gas sensing measurements with low NO gas concentrations in air were performed using an in-house gas sensor testing setup in the temperature range 100-300 °C. On the example of one particular gas concentration, results showed that pseudobrookite exhibited a distinct response to NO already at 150 °C that further improved with increased sample temperature.
Ključne reči:
air / alumina / alumina substrates / anatase / excess rutile / gas concentrations / gas sensing measurements / gas sensors / glass frit / hematite / in-house gas sensor testing setup / interdigitated electrode geometry / low-temperature sensitive material / metals / mixed orthorhombic-monoclinic structure / molar ratio mixture / nanoparticles / nitrogen compounds / nitrogen oxide gas sensors / organic binder / pseudobrookite thick films / resistance / screen printing paste / sintering / starting nanopowders / temperature / temperature measurement / Temperature sensors / thick films / X-ray diffraction / XRD analysisIzvor:
2017 40th International Spring Seminar on Electronics Technology (ISSE), 2017, 1-6Izdavač:
- IEEE
DOI: 10.1109/ISSE.2017.8000881
ISBN: 978-1-5386-0582-0
ISSN: 2161-2536
Scopus: 2-s2.0-85029899359
Institucija/grupa
Институт техничких наука САНУ / Institute of Technical Sciences of SASATY - CONF AU - Mišković, Goran AU - Nikolić, Maria Vesna AU - Luković, Miloljub D. AU - Vasiljević, Zorka Ž. AU - Nicolics, Johann AU - Aleksić, Obrad S. PY - 2017 UR - https://dais.sanu.ac.rs/123456789/3685 AB - Pseudobrookite thick films were obtained by screen printing paste composed of a 1:1.5 molar ratio mixture of starting nanopowders of hematite and anatase, glass frit and organic binder. The films were deposited on alumina substrates with interdigitated electrode geometry. Sintering at 850 °C resulted in the formation of pseudobrookite. X-Ray Diffraction (XRD) analysis showed pseudobrookite with a mixed orthorhombic and monoclinic structure and a small amount of excess rutile. Gas sensing measurements with low NO gas concentrations in air were performed using an in-house gas sensor testing setup in the temperature range 100-300 °C. On the example of one particular gas concentration, results showed that pseudobrookite exhibited a distinct response to NO already at 150 °C that further improved with increased sample temperature. PB - IEEE C3 - 2017 40th International Spring Seminar on Electronics Technology (ISSE) T1 - Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors SP - 1 EP - 6 DO - 10.1109/ISSE.2017.8000881 UR - https://hdl.handle.net/21.15107/rcub_dais_3685 ER -
@conference{ author = "Mišković, Goran and Nikolić, Maria Vesna and Luković, Miloljub D. and Vasiljević, Zorka Ž. and Nicolics, Johann and Aleksić, Obrad S.", year = "2017", abstract = "Pseudobrookite thick films were obtained by screen printing paste composed of a 1:1.5 molar ratio mixture of starting nanopowders of hematite and anatase, glass frit and organic binder. The films were deposited on alumina substrates with interdigitated electrode geometry. Sintering at 850 °C resulted in the formation of pseudobrookite. X-Ray Diffraction (XRD) analysis showed pseudobrookite with a mixed orthorhombic and monoclinic structure and a small amount of excess rutile. Gas sensing measurements with low NO gas concentrations in air were performed using an in-house gas sensor testing setup in the temperature range 100-300 °C. On the example of one particular gas concentration, results showed that pseudobrookite exhibited a distinct response to NO already at 150 °C that further improved with increased sample temperature.", publisher = "IEEE", journal = "2017 40th International Spring Seminar on Electronics Technology (ISSE)", title = "Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors", pages = "1-6", doi = "10.1109/ISSE.2017.8000881", url = "https://hdl.handle.net/21.15107/rcub_dais_3685" }
Mišković, G., Nikolić, M. V., Luković, M. D., Vasiljević, Z. Ž., Nicolics, J.,& Aleksić, O. S.. (2017). Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors. in 2017 40th International Spring Seminar on Electronics Technology (ISSE) IEEE., 1-6. https://doi.org/10.1109/ISSE.2017.8000881 https://hdl.handle.net/21.15107/rcub_dais_3685
Mišković G, Nikolić MV, Luković MD, Vasiljević ZŽ, Nicolics J, Aleksić OS. Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors. in 2017 40th International Spring Seminar on Electronics Technology (ISSE). 2017;:1-6. doi:10.1109/ISSE.2017.8000881 https://hdl.handle.net/21.15107/rcub_dais_3685 .
Mišković, Goran, Nikolić, Maria Vesna, Luković, Miloljub D., Vasiljević, Zorka Ž., Nicolics, Johann, Aleksić, Obrad S., "Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors" in 2017 40th International Spring Seminar on Electronics Technology (ISSE) (2017):1-6, https://doi.org/10.1109/ISSE.2017.8000881 ., https://hdl.handle.net/21.15107/rcub_dais_3685 .
Related items
Showing items related by title, author, creator and subject.
-
Analiza osetljivosti debeloslojnih NTC termistora na promene temperature i protoka vazduha / Analysys of sensitivity of thick film NTC thermistors to temperature and air flow variations
Savić, Slavica M. (Čačak : University of Kragujevac, Faculty of Technical Sciences, 2006) -
Stochastic two-bit on-line temperature measurement with RTD Pt-100 sensor operating in a nonlinear mode
Sovilj, Platon; Vujičić, Bojan; Pejić, Dragan; Radonjić, Aleksandar; Vujičić, Vladimir (International Measurement Confederation, 2020) -
Low temperature sensitivity of upconversion emission in Y2O3:Yb,Tm and Y2O3:Yb,Ho powders
Lojpur, Vesna; Nikolić, Marko G.; Medić, Mina; Mančić, Lidija; Milošević, Olivera; Dramićanin, Miroslav (2nd International Conference on Optical, Electronic and Electrical Materials, 5-7 August 2012, Shanghai, China, 2012)