dc.description.abstractAn injectable polydimethylsiloxane/hydroxyapatite (PDMS/HAp) composite cement was synthesised using linear PDMS and HAp (particles of about 100 nm in size) of different mass fractions. The effect of HAp mass fraction (5-60 mass%) on the hardness of PDMS/HAp composite cement was investigated. The hardness achieved is 25-49degreesShA. Differential scanning calorimetry (DSC) was used to study the cross-linking process and the influence of HAp on the temperature and duration of PDMS/HAp cross-linking. The microstructure of composite cement surfaces after 10 days in vivo tests was observed by scanning electron microscopy (SEM). The presence of well-adhered macrophages, fibroblasts and monocytes was found on the implant surface upon its extraction from the organism.en
dc.rightsrestrictedAccessen
dc.sourceBio-Medical Materials and Engineeringen
dc.subjectcomposite cementen
dc.subjectpolydimethylsiloxane/hydroxyapatiteen
dc.subjecthardnessen
dc.subjectcross-linkingen
dc.subjectin vivo testen
dc.titleInjectable polydimethylsiloxane-hydroxyapatite composite cementen
dc.typearticleen
dc.rights.licenseARR
dcterms.abstractЈовановиц, Јелена; Игњатовић, Ненад; Суљоврујић, Един Х.; Ускоковић, Драган;
dc.citation.spage401
dc.citation.epage410
dc.citation.volume13
dc.citation.issue4
dc.identifier.wos000186789900009
dc.identifier.pmid14646054
dc.type.versionpublishedVersion
dc.identifier.rcubhttps://hdl.handle.net/21.15107/rcub_dais_2748


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу