AB  - In this study, microstructure evolution and dielectric properties of SrTiO3 ceramic have been investigated, whereby mechanical activation of SrTiO3 powders was used to modify the functional properties of ceramic materials. Microstructural SEM analysis of SrTiO3 ceramics showed that the increase in mechanical activation time results in less porous samples. Raman spectroscopy indicated changes in the broadening and asymmetry of the TO2 mode with a change in the time of mechanical activation. TO2 mode showed a Fano asymmetry due to its interaction with polarization fluctuations in polar micro-regions, which are a consequence of the presence of oxygen vacancies caused by activation. The maximum value of dielectric permittivity was observed in the sample activated for 10 min. Also, the sample activated for 10 min exhibits relatively low values of loss tangent, compared to the other mechanically activated samples, providing the best overall dielectric performance compared to other samples.
T2  - Science of Sintering
T1  - Dielectric Properties of Mechanically Activated Strontium Titanate Ceramics
SP  - 401
EP  - 414
VL  - 54
IS  - 4
DO  - 10.2298/SOS2204401Z
UR  - https://hdl.handle.net/21.15107/rcub_dais_13510
ER  - 

@article{
author = "Živojinović, Jelena and Kosanović, Darko and Blagojević, Vladimir A. and Pavlović, Vera P. and Tadić, Nenad and Vlahović, Branislav and Pavlović, Vladimir B.",
year = "2022",
abstract = "In this study, microstructure evolution and dielectric properties of SrTiO3 ceramic have been investigated, whereby mechanical activation of SrTiO3 powders was used to modify the functional properties of ceramic materials. Microstructural SEM analysis of SrTiO3 ceramics showed that the increase in mechanical activation time results in less porous samples. Raman spectroscopy indicated changes in the broadening and asymmetry of the TO2 mode with a change in the time of mechanical activation. TO2 mode showed a Fano asymmetry due to its interaction with polarization fluctuations in polar micro-regions, which are a consequence of the presence of oxygen vacancies caused by activation. The maximum value of dielectric permittivity was observed in the sample activated for 10 min. Also, the sample activated for 10 min exhibits relatively low values of loss tangent, compared to the other mechanically activated samples, providing the best overall dielectric performance compared to other samples.",
journal = "Science of Sintering",
title = "Dielectric Properties of Mechanically Activated Strontium Titanate Ceramics",
pages = "401-414",
volume = "54",
number = "4",
doi = "10.2298/SOS2204401Z",
url = "https://hdl.handle.net/21.15107/rcub_dais_13510"
}

Živojinović, J., Kosanović, D., Blagojević, V. A., Pavlović, V. P., Tadić, N., Vlahović, B.,& Pavlović, V. B.. (2022). Dielectric Properties of Mechanically Activated Strontium Titanate Ceramics. in Science of Sintering, 54(4), 401-414.
https://doi.org/10.2298/SOS2204401Z
https://hdl.handle.net/21.15107/rcub_dais_13510

Živojinović J, Kosanović D, Blagojević VA, Pavlović VP, Tadić N, Vlahović B, Pavlović VB. Dielectric Properties of Mechanically Activated Strontium Titanate Ceramics. in Science of Sintering. 2022;54(4):401-414.
doi:10.2298/SOS2204401Z
https://hdl.handle.net/21.15107/rcub_dais_13510 .

Živojinović, Jelena, Kosanović, Darko, Blagojević, Vladimir A., Pavlović, Vera P., Tadić, Nenad, Vlahović, Branislav, Pavlović, Vladimir B., "Dielectric Properties of Mechanically Activated Strontium Titanate Ceramics" in Science of Sintering, 54, no. 4 (2022):401-414,
https://doi.org/10.2298/SOS2204401Z .,
https://hdl.handle.net/21.15107/rcub_dais_13510 .