abstract = "The thermal properties of zirconium diboride (ZrB2) ceramics with tungsten additions of up to 5 wt% were characterized up to 2000°C. Densification was promoted by the addition of 0.5 wt% carbon. ZrB2 ceramics were prepared from commercially available powder by hot pressing. The crystalline phases present were determined by x-ray diffraction. The microstructure and density change as a result of the addition of tungsten, but this does not affect much the thermal behavior of ZrB2 at room and elevated temperatures. Thermal diffusivity at 200°C decreased from 0.158 cm2/s for nominally pure ZrB2 to 0.149 cm2/s for ZrB2 with 5 wt% Tungsten carbide (WC). The thermal diffusivity decreased with increasing temperature, reaching a value of 0.145 cm2/s at 2000°C for ZrB2 with 5 wt% Tungsten carbide (WC). Heat capacity, unlike thermal diffusivity, did not change during thermal cycling. Thermal conductivity, which was calculated from thermal diffusivity, heat capacity, and density, was as high as 77.9 W/(m·K) at 2000°C for ZrB2 with 5 wt% Tungsten carbide (WC). Any level of Tungsten carbide (WC) contamination reduces thermal conductivity. Properties, including hardness, oxygen content, elastic modulus, strength were measured and will be discussed.",
publisher = "Belgrade : University of Belgrade - Faculty of Mechanical Engineering",
journal = "Programme and The Book of Abstracts / International Conference of Experimental and Numerical Investigations and New Technologies - CNN TECH 2023, 04 – 07 July 2023, Zlatibor, Serbia",
title = "Elevated Temperature Thermal Properties of ZrB2 with Tungsten Additions",
pages = "79",
url = "https://hdl.handle.net/21.15107/rcub_dais_15009"
}