TY  - JOUR
AU  - Marković, Smilja
AU  - Rau, Julietta V.
AU  - De Bonis, Angela
AU  - De Bellis, Giovanni
AU  - Stojanović, Zoran
AU  - Veselinović, Ljiljana
AU  - Mitrić, Miodrag
AU  - Ignjatović, Nenad
AU  - Škapin, Srečo Davor
AU  - Vengust, Damjan
PY  - 2022
UR  - https://dais.sanu.ac.rs/123456789/12953
AB  - Dense calcium phosphate-based ceramics were fabricated to be used as targets for pulsed laser deposition (PLD). Nanostructured cobalt-substituted hydroxyapatite (Co:HAP) was used as a starting powder. To vary phase composition and microstructure of targets, two sintering approaches were applied, conventional (CS) and two-step sintering (TSS). The obtained results show that in both cases biphasic calcium phosphate (BCP) ceramics (targets) were prepared, with slightly different HAP-to-β–TCP amount ratio and a significantly different microstructure. While the CS method yielded fully dense ceramics with an average grain size of 1.3 μm, the ceramics prepared by TSS had a density of 98.5%, with a predominant grain size below 100 nm. (Ca + Co)P coatings were prepared by PLD of (Ca + Co)P targets. The temperature of the Ti substrate was adjusted to be 25 and 500 °C. The results show that the phase composition of (Ca + Co)P coatings depended on the phase composition of targets as well as on the temperature of the Ti substrate. The coating prepared at 25 °C using CS target consisted of three calcium phosphate phases, HAP, β–TCP and α–TCP; when the TSS target was used, the coating was biphasic, containing HAP and β–TCP. When the substrate was heated to 500 °C, regardless of whether the CS or the TSS target was used, the deposited coatings were composed of HAP and α–TCP. Due to different phase compositions, the (Ca + Co)P coatings deposited at 25 °C showed an improved hardness compared to those deposited at 500 °C. The obtained results confirmed that the phase composition, morphology and mechanical properties of 0.3 μm thick (Ca + Co)P coatings on a Ti substrate can be tailored by employing (Ca + Co)P targets with different microstructures, and also by varying the temperature of the Ti substrate during deposition experiments.
T2  - Surface and Coatings Technology
T2  - Surface and Coatings TechnologySurface and Coatings Technology
T1  - Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium
SP  - 128275
VL  - 437
DO  - 10.1016/j.surfcoat.2022.128275
UR  - https://hdl.handle.net/21.15107/rcub_dais_12953
ER  - 

@article{
author = "Marković, Smilja and Rau, Julietta V. and De Bonis, Angela and De Bellis, Giovanni and Stojanović, Zoran and Veselinović, Ljiljana and Mitrić, Miodrag and Ignjatović, Nenad and Škapin, Srečo Davor and Vengust, Damjan",
year = "2022",
abstract = "Dense calcium phosphate-based ceramics were fabricated to be used as targets for pulsed laser deposition (PLD). Nanostructured cobalt-substituted hydroxyapatite (Co:HAP) was used as a starting powder. To vary phase composition and microstructure of targets, two sintering approaches were applied, conventional (CS) and two-step sintering (TSS). The obtained results show that in both cases biphasic calcium phosphate (BCP) ceramics (targets) were prepared, with slightly different HAP-to-β–TCP amount ratio and a significantly different microstructure. While the CS method yielded fully dense ceramics with an average grain size of 1.3 μm, the ceramics prepared by TSS had a density of 98.5%, with a predominant grain size below 100 nm. (Ca + Co)P coatings were prepared by PLD of (Ca + Co)P targets. The temperature of the Ti substrate was adjusted to be 25 and 500 °C. The results show that the phase composition of (Ca + Co)P coatings depended on the phase composition of targets as well as on the temperature of the Ti substrate. The coating prepared at 25 °C using CS target consisted of three calcium phosphate phases, HAP, β–TCP and α–TCP; when the TSS target was used, the coating was biphasic, containing HAP and β–TCP. When the substrate was heated to 500 °C, regardless of whether the CS or the TSS target was used, the deposited coatings were composed of HAP and α–TCP. Due to different phase compositions, the (Ca + Co)P coatings deposited at 25 °C showed an improved hardness compared to those deposited at 500 °C. The obtained results confirmed that the phase composition, morphology and mechanical properties of 0.3 μm thick (Ca + Co)P coatings on a Ti substrate can be tailored by employing (Ca + Co)P targets with different microstructures, and also by varying the temperature of the Ti substrate during deposition experiments.",
journal = "Surface and Coatings Technology, Surface and Coatings TechnologySurface and Coatings Technology",
title = "Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium",
pages = "128275",
volume = "437",
doi = "10.1016/j.surfcoat.2022.128275",
url = "https://hdl.handle.net/21.15107/rcub_dais_12953"
}

Marković, S., Rau, J. V., De Bonis, A., De Bellis, G., Stojanović, Z., Veselinović, L., Mitrić, M., Ignjatović, N., Škapin, S. D.,& Vengust, D.. (2022). Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium. in Surface and Coatings Technology, 437, 128275.
https://doi.org/10.1016/j.surfcoat.2022.128275
https://hdl.handle.net/21.15107/rcub_dais_12953

Marković S, Rau JV, De Bonis A, De Bellis G, Stojanović Z, Veselinović L, Mitrić M, Ignjatović N, Škapin SD, Vengust D. Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium. in Surface and Coatings Technology. 2022;437:128275.
doi:10.1016/j.surfcoat.2022.128275
https://hdl.handle.net/21.15107/rcub_dais_12953 .

Marković, Smilja, Rau, Julietta V., De Bonis, Angela, De Bellis, Giovanni, Stojanović, Zoran, Veselinović, Ljiljana, Mitrić, Miodrag, Ignjatović, Nenad, Škapin, Srečo Davor, Vengust, Damjan, "Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium" in Surface and Coatings Technology, 437 (2022):128275,
https://doi.org/10.1016/j.surfcoat.2022.128275 .,
https://hdl.handle.net/21.15107/rcub_dais_12953 .

TY  - JOUR
AU  - Marković, Smilja
AU  - Rau, Julietta V.
AU  - De Bonis, Angela
AU  - De Bellis, Giovanni
AU  - Stojanović, Zoran
AU  - Veselinović, Ljiljana
AU  - Mitrić, Miodrag
AU  - Ignjatović, Nenad
AU  - Škapin, Srečo Davor
AU  - Vengust, Damjan
PY  - 2022
UR  - https://dais.sanu.ac.rs/123456789/13034
AB  - Dense calcium phosphate-based ceramics were fabricated to be used as targets for pulsed laser deposition (PLD). Nanostructured cobalt-substituted hydroxyapatite (Co:HAP) was used as a starting powder. To vary phase composition and microstructure of targets, two sintering approaches were applied, conventional (CS) and two-step sintering (TSS). The obtained results show that in both cases biphasic calcium phosphate (BCP) ceramics (targets) were prepared, with slightly different HAP-to-β–TCP amount ratio and a significantly different microstructure. While the CS method yielded fully dense ceramics with an average grain size of 1.3 μm, the ceramics prepared by TSS had a density of 98.5%, with a predominant grain size below 100 nm. (Ca + Co)P coatings were prepared by PLD of (Ca + Co)P targets. The temperature of the Ti substrate was adjusted to be 25 and 500 °C. The results show that the phase composition of (Ca + Co)P coatings depended on the phase composition of targets as well as on the temperature of the Ti substrate. The coating prepared at 25 °C using CS target consisted of three calcium phosphate phases, HAP, β–TCP and α–TCP; when the TSS target was used, the coating was biphasic, containing HAP and β–TCP. When the substrate was heated to 500 °C, regardless of whether the CS or the TSS target was used, the deposited coatings were composed of HAP and α–TCP. Due to different phase compositions, the (Ca + Co)P coatings deposited at 25 °C showed an improved hardness compared to those deposited at 500 °C. The obtained results confirmed that the phase composition, morphology and mechanical properties of 0.3 μm thick (Ca + Co)P coatings on a Ti substrate can be tailored by employing (Ca + Co)P targets with different microstructures, and also by varying the temperature of the Ti substrate during deposition experiments.
T2  - Surface and Coatings Technology
T1  - Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium
SP  - 128275
VL  - 437
DO  - 10.1016/j.surfcoat.2022.128275
UR  - https://hdl.handle.net/21.15107/rcub_dais_13034
ER  - 

@article{
author = "Marković, Smilja and Rau, Julietta V. and De Bonis, Angela and De Bellis, Giovanni and Stojanović, Zoran and Veselinović, Ljiljana and Mitrić, Miodrag and Ignjatović, Nenad and Škapin, Srečo Davor and Vengust, Damjan",
year = "2022",
abstract = "Dense calcium phosphate-based ceramics were fabricated to be used as targets for pulsed laser deposition (PLD). Nanostructured cobalt-substituted hydroxyapatite (Co:HAP) was used as a starting powder. To vary phase composition and microstructure of targets, two sintering approaches were applied, conventional (CS) and two-step sintering (TSS). The obtained results show that in both cases biphasic calcium phosphate (BCP) ceramics (targets) were prepared, with slightly different HAP-to-β–TCP amount ratio and a significantly different microstructure. While the CS method yielded fully dense ceramics with an average grain size of 1.3 μm, the ceramics prepared by TSS had a density of 98.5%, with a predominant grain size below 100 nm. (Ca + Co)P coatings were prepared by PLD of (Ca + Co)P targets. The temperature of the Ti substrate was adjusted to be 25 and 500 °C. The results show that the phase composition of (Ca + Co)P coatings depended on the phase composition of targets as well as on the temperature of the Ti substrate. The coating prepared at 25 °C using CS target consisted of three calcium phosphate phases, HAP, β–TCP and α–TCP; when the TSS target was used, the coating was biphasic, containing HAP and β–TCP. When the substrate was heated to 500 °C, regardless of whether the CS or the TSS target was used, the deposited coatings were composed of HAP and α–TCP. Due to different phase compositions, the (Ca + Co)P coatings deposited at 25 °C showed an improved hardness compared to those deposited at 500 °C. The obtained results confirmed that the phase composition, morphology and mechanical properties of 0.3 μm thick (Ca + Co)P coatings on a Ti substrate can be tailored by employing (Ca + Co)P targets with different microstructures, and also by varying the temperature of the Ti substrate during deposition experiments.",
journal = "Surface and Coatings Technology",
title = "Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium",
pages = "128275",
volume = "437",
doi = "10.1016/j.surfcoat.2022.128275",
url = "https://hdl.handle.net/21.15107/rcub_dais_13034"
}

Marković, S., Rau, J. V., De Bonis, A., De Bellis, G., Stojanović, Z., Veselinović, L., Mitrić, M., Ignjatović, N., Škapin, S. D.,& Vengust, D.. (2022). Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium. in Surface and Coatings Technology, 437, 128275.
https://doi.org/10.1016/j.surfcoat.2022.128275
https://hdl.handle.net/21.15107/rcub_dais_13034

Marković S, Rau JV, De Bonis A, De Bellis G, Stojanović Z, Veselinović L, Mitrić M, Ignjatović N, Škapin SD, Vengust D. Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium. in Surface and Coatings Technology. 2022;437:128275.
doi:10.1016/j.surfcoat.2022.128275
https://hdl.handle.net/21.15107/rcub_dais_13034 .

Marković, Smilja, Rau, Julietta V., De Bonis, Angela, De Bellis, Giovanni, Stojanović, Zoran, Veselinović, Ljiljana, Mitrić, Miodrag, Ignjatović, Nenad, Škapin, Srečo Davor, Vengust, Damjan, "Pathway to tailor the phase composition, microstructure and mechanical properties of pulsed laser deposited cobalt-substituted calcium phosphate coatings on titanium" in Surface and Coatings Technology, 437 (2022):128275,
https://doi.org/10.1016/j.surfcoat.2022.128275 .,
https://hdl.handle.net/21.15107/rcub_dais_13034 .