@article{
author = "Veselinović, Ljiljana and Mitrić, Miodrag and Avdeev, Maxim and Marković, Smilja and Uskoković, Dragan",
year = "2016",
abstract = "Neutron powder diffraction (NPD) was employed to further investigate the BaTi1−xSnxO3 (BTS) system previously studied by X-ray diffraction. The room-temperature phase compositions and crystal structures of BTS samples with x = 0, 0.025, 0.05, 0.07, 0.10, 0.12, 0.15 and 0.20 were refined by the Rietveld method using NPD data. It is well known that barium titanate powder (x = 0) crystallizes in the tetragonal P4mm space group. The crystal structures of the samples with 0.025 ≤ x ≤ 0.07 were refined as mixtures of P4mm and Amm2 phases; those with x = 0.1 and 0.12 show the coexistence of rhombohedral R3m and cubic phases, while the samples with x = 0.15 and 0.20 crystallize in a single cubic [Pm3m] phase. Temperature-dependent NPD was used to characterize the BaTi0.95Sn0.05O3 sample at 273, 333 and 373 K, and it was found to form single-phase Amm2, P4mm and [Pm3m] structures at these respective temperatures. The NPD results are in agreement with data obtained by differential scanning calorimetry and dielectric permittivity measurements, which show a paraelectric–ferroelectric transition (associated with structural transition) from [Pm3m] to P4mm at about 353 K followed by a P4mm to Amm2 phase transition at about 303 K.",
publisher = "International Union of Crystallography",
journal = "Journal of Applied Crystallography",
title = "New insights into BaTi1–xSnxO3 (0 ≤ x ≤ 0.20) phase diagram from neutron diffraction data",
pages = "1726-1733",
volume = "49",
doi = "10.1107/S1600576716013157",
url = "https://hdl.handle.net/21.15107/rcub_dais_2328"
}