TY  - CONF
AU  - Kesić, Željka
AU  - Lukić, Ivana
AU  - Zdujić, Miodrag
AU  - Jovalekić, Čedomir
AU  - Shao, Yong
AU  - Liu, Hui
AU  - Skala, Dejan
PY  - 2013
UR  - https://dais.sanu.ac.rs/123456789/423
AB  - The mixed oxide of CaO·ZnO and K2CO3 were prepared by ball milling of CaO and ZnO powders and water, with addition of K2CO3 and afterward by calcination at 700 oC. Influence of different molar ratio of K2CO3 and CaO (x=1, 2 and 4 moles of K2CO3 per 10 moles of CaO) was studied . The prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning
electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and the particle size laser diffraction (PSLD) distribution. The addition of smaller amount of K2CO3 at the beginning of ball miling (x≤2), favors the formation of calcium zinc hydroxide hydrate, while it is not the case when K2CO3 larger addition was used (x > 2). A larger amount of potassium carbonate in the initial
composition of powder mixture negatively affected formation of CaZn2(OH)6·2H2O. Bimodal distribution were detected for all samples after calcination at 700 oC and the results showed that the distribution of elements in the bulk is not homogeneous and that surface of formed mixed oxide CaO.ZnO (XPS analysis) after calcination is mainly covered by potassium species. That evidence indicate that the K2CO3 was not fully incorporated into the matrix. Prepared samples could be used for methanolysis of vegetable oil and fatty acid methyl esters (FAME, i.e. biodiesel) synthesis.
PB  - Belgrade : Serbian Ceramic Society
C3  - Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
T1  - Biodiesel synthesis based on CaO·ZnO.K2CO3 as catalyst
SP  - 46
EP  - 46
UR  - https://hdl.handle.net/21.15107/rcub_dais_423
ER  - 

@conference{
author = "Kesić, Željka and Lukić, Ivana and Zdujić, Miodrag and Jovalekić, Čedomir and Shao, Yong and Liu, Hui and Skala, Dejan",
year = "2013",
abstract = "The mixed oxide of CaO·ZnO and K2CO3 were prepared by ball milling of CaO and ZnO powders and water, with addition of K2CO3 and afterward by calcination at 700 oC. Influence of different molar ratio of K2CO3 and CaO (x=1, 2 and 4 moles of K2CO3 per 10 moles of CaO) was studied . The prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning
electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and the particle size laser diffraction (PSLD) distribution. The addition of smaller amount of K2CO3 at the beginning of ball miling (x≤2), favors the formation of calcium zinc hydroxide hydrate, while it is not the case when K2CO3 larger addition was used (x > 2). A larger amount of potassium carbonate in the initial
composition of powder mixture negatively affected formation of CaZn2(OH)6·2H2O. Bimodal distribution were detected for all samples after calcination at 700 oC and the results showed that the distribution of elements in the bulk is not homogeneous and that surface of formed mixed oxide CaO.ZnO (XPS analysis) after calcination is mainly covered by potassium species. That evidence indicate that the K2CO3 was not fully incorporated into the matrix. Prepared samples could be used for methanolysis of vegetable oil and fatty acid methyl esters (FAME, i.e. biodiesel) synthesis.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade",
title = "Biodiesel synthesis based on CaO·ZnO.K2CO3 as catalyst",
pages = "46-46",
url = "https://hdl.handle.net/21.15107/rcub_dais_423"
}

Kesić, Ž., Lukić, I., Zdujić, M., Jovalekić, Č., Shao, Y., Liu, H.,& Skala, D.. (2013). Biodiesel synthesis based on CaO·ZnO.K2CO3 as catalyst. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
Belgrade : Serbian Ceramic Society., 46-46.
https://hdl.handle.net/21.15107/rcub_dais_423

Kesić Ž, Lukić I, Zdujić M, Jovalekić Č, Shao Y, Liu H, Skala D. Biodiesel synthesis based on CaO·ZnO.K2CO3 as catalyst. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade. 2013;:46-46.
https://hdl.handle.net/21.15107/rcub_dais_423 .

Kesić, Željka, Lukić, Ivana, Zdujić, Miodrag, Jovalekić, Čedomir, Shao, Yong, Liu, Hui, Skala, Dejan, "Biodiesel synthesis based on CaO·ZnO.K2CO3 as catalyst" in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade (2013):46-46,
https://hdl.handle.net/21.15107/rcub_dais_423 .

TY  - CONF
AU  - Kesić, Željka
AU  - Lukić, Ivana
AU  - Zdujić, Miodrag
AU  - Jovalekić, Čedomir
AU  - Shao, Yong
AU  - Liu, Hui
AU  - Skala, Dejan
PY  - 2013
UR  - https://dais.sanu.ac.rs/123456789/422
AB  - The mixed oxide of CaO·ZnO and K2CO3 were prepared by ball milling of CaO and ZnO powders and water, with addition of K2CO3 and afterward by calcination at 700 oC. Influence of different molar ratio of K2CO3 and CaO (x=1, 2 and 4 moles of K2CO3 per 10 moles of CaO) was studied . The prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and the particle size laser diffraction (PSLD) distribution. The addition of smaller amount of K2CO3 at the beginning of ball miling (x≤2), favors the formation of calcium zinc hydroxide hydrate, while it is not the case when K2CO3 larger addition was used (x > 2). A larger amount of potassium carbonate in the initial composition of powder mixture negatively affected formation of CaZn2(OH)6·2H2O. Bimodal distribution were detected for all samples after calcination at 700 oC and the results showed that the distribution of elements in the bulk is not homogeneous and that surface of formed mixed oxide CaO.ZnO (XPS analysis) after calcination is mainly covered by potassium species. That evidence indicate that the K2CO3 was not fully incorporated into the matrix. Prepared samples could be used for methanolysis of vegetable oil and fatty acid methyl esters (FAME, i.e. biodiesel) synthesis.
PB  - Belgrade : Serbian Ceramic Society
C3  - Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
T1  - Characterization of mechanochemically synthesized CaO·ZnO.K2CO3
SP  - 45
EP  - 45
UR  - https://hdl.handle.net/21.15107/rcub_dais_422
ER  - 

@conference{
author = "Kesić, Željka and Lukić, Ivana and Zdujić, Miodrag and Jovalekić, Čedomir and Shao, Yong and Liu, Hui and Skala, Dejan",
year = "2013",
abstract = "The mixed oxide of CaO·ZnO and K2CO3 were prepared by ball milling of CaO and ZnO powders and water, with addition of K2CO3 and afterward by calcination at 700 oC. Influence of different molar ratio of K2CO3 and CaO (x=1, 2 and 4 moles of K2CO3 per 10 moles of CaO) was studied . The prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), infrared spectroscopy (FTIR), scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and the particle size laser diffraction (PSLD) distribution. The addition of smaller amount of K2CO3 at the beginning of ball miling (x≤2), favors the formation of calcium zinc hydroxide hydrate, while it is not the case when K2CO3 larger addition was used (x > 2). A larger amount of potassium carbonate in the initial composition of powder mixture negatively affected formation of CaZn2(OH)6·2H2O. Bimodal distribution were detected for all samples after calcination at 700 oC and the results showed that the distribution of elements in the bulk is not homogeneous and that surface of formed mixed oxide CaO.ZnO (XPS analysis) after calcination is mainly covered by potassium species. That evidence indicate that the K2CO3 was not fully incorporated into the matrix. Prepared samples could be used for methanolysis of vegetable oil and fatty acid methyl esters (FAME, i.e. biodiesel) synthesis.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade",
title = "Characterization of mechanochemically synthesized CaO·ZnO.K2CO3",
pages = "45-45",
url = "https://hdl.handle.net/21.15107/rcub_dais_422"
}

Kesić, Ž., Lukić, I., Zdujić, M., Jovalekić, Č., Shao, Y., Liu, H.,& Skala, D.. (2013). Characterization of mechanochemically synthesized CaO·ZnO.K2CO3. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade
Belgrade : Serbian Ceramic Society., 45-45.
https://hdl.handle.net/21.15107/rcub_dais_422

Kesić Ž, Lukić I, Zdujić M, Jovalekić Č, Shao Y, Liu H, Skala D. Characterization of mechanochemically synthesized CaO·ZnO.K2CO3. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade. 2013;:45-45.
https://hdl.handle.net/21.15107/rcub_dais_422 .

Kesić, Željka, Lukić, Ivana, Zdujić, Miodrag, Jovalekić, Čedomir, Shao, Yong, Liu, Hui, Skala, Dejan, "Characterization of mechanochemically synthesized CaO·ZnO.K2CO3" in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts : II Serbian Ceramic Society Conference, Sep 30th-Oct 1st, 2013, Belgrade (2013):45-45,
https://hdl.handle.net/21.15107/rcub_dais_422 .