TY  - JOUR
AU  - Kosanović, Darko
AU  - Blagojević, Vladimir A.
AU  - Maričić, Aleksa
AU  - Aleksić, S.
AU  - Pavlović, Vera P.
AU  - Pavlović, Vladimir B.
AU  - Vlahović, Branislav
PY  - 2018
UR  - https://dais.sanu.ac.rs/123456789/3742
AB  - Barium hexaferrite ceramics were prepared using mechanically activated mixtures of iron and barium titanate. The 60:40 mass% Fe:BaTiO3 powder mixtures were mechanically activated for different times (100–240 min) and sintered at 1100 and 1200 °C in order to determine the influence of mechanical activation of the precursor on the magnetic and dielectric properties of the resulting barium hexaferrite ceramics. The final product contained 84–89 mass% of Ba2Fe22.46O38Ti1.54 phase, with higher content corresponding to longer mechanical activation of the precursor. XRD and Raman measurements indicated that the remainder of the sample consists of leftover BaTiO3 and hematite, which was formed by the oxidation of iron during mechanical activation and sintering in air. Magnetic properties of samples sintered at 1200 °C are superior to those sintered at 1100 °C, which can be attributed to higher Ba2Fe22.46O38Ti1.54 phase content. The position of the Curie temperature in 350–420 °C temperature region is consistent with 0.8:1 ratio of Ti to Ba. Maximum magnetization was observed for samples activated for 120 min. Dielectric properties of samples sintered at 1200 °C showed a dependence on frequency, with a significant drop in relative permittivity with an increase in frequency in the low-frequency region, and relatively constant values of relative permittivity in the high-frequency region. The tangent loss showed a decrease with increase in frequency, where peaks corresponding to the resonance of the electron hopping frequency with the external field were observed in the samples corresponding to the longer mechanical activation. Dielectric properties showed relatively small changes for samples activated longer than 150 min. © 2018 Elsevier Ltd and Techna Group S.r.l.
PB  - Elsevier
T2  - Ceramics International
T1  - Influence of mechanical activation on functional properties of barium hexaferrite ceramics
SP  - 6666
EP  - 6672
VL  - 44
IS  - 6
DO  - 10.1016/j.ceramint.2018.01.078
UR  - https://hdl.handle.net/21.15107/rcub_dais_3742
ER  - 

@article{
author = "Kosanović, Darko and Blagojević, Vladimir A. and Maričić, Aleksa and Aleksić, S. and Pavlović, Vera P. and Pavlović, Vladimir B. and Vlahović, Branislav",
year = "2018",
abstract = "Barium hexaferrite ceramics were prepared using mechanically activated mixtures of iron and barium titanate. The 60:40 mass% Fe:BaTiO3 powder mixtures were mechanically activated for different times (100–240 min) and sintered at 1100 and 1200 °C in order to determine the influence of mechanical activation of the precursor on the magnetic and dielectric properties of the resulting barium hexaferrite ceramics. The final product contained 84–89 mass% of Ba2Fe22.46O38Ti1.54 phase, with higher content corresponding to longer mechanical activation of the precursor. XRD and Raman measurements indicated that the remainder of the sample consists of leftover BaTiO3 and hematite, which was formed by the oxidation of iron during mechanical activation and sintering in air. Magnetic properties of samples sintered at 1200 °C are superior to those sintered at 1100 °C, which can be attributed to higher Ba2Fe22.46O38Ti1.54 phase content. The position of the Curie temperature in 350–420 °C temperature region is consistent with 0.8:1 ratio of Ti to Ba. Maximum magnetization was observed for samples activated for 120 min. Dielectric properties of samples sintered at 1200 °C showed a dependence on frequency, with a significant drop in relative permittivity with an increase in frequency in the low-frequency region, and relatively constant values of relative permittivity in the high-frequency region. The tangent loss showed a decrease with increase in frequency, where peaks corresponding to the resonance of the electron hopping frequency with the external field were observed in the samples corresponding to the longer mechanical activation. Dielectric properties showed relatively small changes for samples activated longer than 150 min. © 2018 Elsevier Ltd and Techna Group S.r.l.",
publisher = "Elsevier",
journal = "Ceramics International",
title = "Influence of mechanical activation on functional properties of barium hexaferrite ceramics",
pages = "6666-6672",
volume = "44",
number = "6",
doi = "10.1016/j.ceramint.2018.01.078",
url = "https://hdl.handle.net/21.15107/rcub_dais_3742"
}

Kosanović, D., Blagojević, V. A., Maričić, A., Aleksić, S., Pavlović, V. P., Pavlović, V. B.,& Vlahović, B.. (2018). Influence of mechanical activation on functional properties of barium hexaferrite ceramics. in Ceramics International
Elsevier., 44(6), 6666-6672.
https://doi.org/10.1016/j.ceramint.2018.01.078
https://hdl.handle.net/21.15107/rcub_dais_3742

Kosanović D, Blagojević VA, Maričić A, Aleksić S, Pavlović VP, Pavlović VB, Vlahović B. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. in Ceramics International. 2018;44(6):6666-6672.
doi:10.1016/j.ceramint.2018.01.078
https://hdl.handle.net/21.15107/rcub_dais_3742 .

Kosanović, Darko, Blagojević, Vladimir A., Maričić, Aleksa, Aleksić, S., Pavlović, Vera P., Pavlović, Vladimir B., Vlahović, Branislav, "Influence of mechanical activation on functional properties of barium hexaferrite ceramics" in Ceramics International, 44, no. 6 (2018):6666-6672,
https://doi.org/10.1016/j.ceramint.2018.01.078 .,
https://hdl.handle.net/21.15107/rcub_dais_3742 .

TY  - JOUR
AU  - Kosanović, Darko
AU  - Blagojević, Vladimir A.
AU  - Maričić, Aleksa
AU  - Aleksić, S.
AU  - Pavlović, Vera P.
AU  - Pavlović, Vladimir B.
AU  - Vlahović, Branislav
PY  - 2018
UR  - https://dais.sanu.ac.rs/123456789/4606
AB  - Barium hexaferrite ceramics were prepared using mechanically activated mixtures of iron and barium titanate. The 60:40 mass% Fe:BaTiO3 powder mixtures were mechanically activated for different times (100–240 min) and sintered at 1100 and 1200 °C in order to determine the influence of mechanical activation of the precursor on the magnetic and dielectric properties of the resulting barium hexaferrite ceramics. The final product contained 84–89 mass% of Ba2Fe22.46O38Ti1.54 phase, with higher content corresponding to longer mechanical activation of the precursor. XRD and Raman measurements indicated that the remainder of the sample consists of leftover BaTiO3 and hematite, which was formed by the oxidation of iron during mechanical activation and sintering in air. Magnetic properties of samples sintered at 1200 °C are superior to those sintered at 1100 °C, which can be attributed to higher Ba2Fe22.46O38Ti1.54 phase content. The position of the Curie temperature in 350–420 °C temperature region is consistent with 0.8:1 ratio of Ti to Ba. Maximum magnetization was observed for samples activated for 120 min. Dielectric properties of samples sintered at 1200 °C showed a dependence on frequency, with a significant drop in relative permittivity with an increase in frequency in the low-frequency region, and relatively constant values of relative permittivity in the high-frequency region. The tangent loss showed a decrease with increase in frequency, where peaks corresponding to the resonance of the electron hopping frequency with the external field were observed in the samples corresponding to the longer mechanical activation. Dielectric properties showed relatively small changes for samples activated longer than 150 min. © 2018 Elsevier Ltd and Techna Group S.r.l.
PB  - Elsevier
T2  - Ceramics International
T1  - Influence of mechanical activation on functional properties of barium hexaferrite ceramics
SP  - 6666
EP  - 6672
VL  - 44
IS  - 6
DO  - 10.1016/j.ceramint.2018.01.078
UR  - https://hdl.handle.net/21.15107/rcub_dais_4606
ER  - 

@article{
author = "Kosanović, Darko and Blagojević, Vladimir A. and Maričić, Aleksa and Aleksić, S. and Pavlović, Vera P. and Pavlović, Vladimir B. and Vlahović, Branislav",
year = "2018",
abstract = "Barium hexaferrite ceramics were prepared using mechanically activated mixtures of iron and barium titanate. The 60:40 mass% Fe:BaTiO3 powder mixtures were mechanically activated for different times (100–240 min) and sintered at 1100 and 1200 °C in order to determine the influence of mechanical activation of the precursor on the magnetic and dielectric properties of the resulting barium hexaferrite ceramics. The final product contained 84–89 mass% of Ba2Fe22.46O38Ti1.54 phase, with higher content corresponding to longer mechanical activation of the precursor. XRD and Raman measurements indicated that the remainder of the sample consists of leftover BaTiO3 and hematite, which was formed by the oxidation of iron during mechanical activation and sintering in air. Magnetic properties of samples sintered at 1200 °C are superior to those sintered at 1100 °C, which can be attributed to higher Ba2Fe22.46O38Ti1.54 phase content. The position of the Curie temperature in 350–420 °C temperature region is consistent with 0.8:1 ratio of Ti to Ba. Maximum magnetization was observed for samples activated for 120 min. Dielectric properties of samples sintered at 1200 °C showed a dependence on frequency, with a significant drop in relative permittivity with an increase in frequency in the low-frequency region, and relatively constant values of relative permittivity in the high-frequency region. The tangent loss showed a decrease with increase in frequency, where peaks corresponding to the resonance of the electron hopping frequency with the external field were observed in the samples corresponding to the longer mechanical activation. Dielectric properties showed relatively small changes for samples activated longer than 150 min. © 2018 Elsevier Ltd and Techna Group S.r.l.",
publisher = "Elsevier",
journal = "Ceramics International",
title = "Influence of mechanical activation on functional properties of barium hexaferrite ceramics",
pages = "6666-6672",
volume = "44",
number = "6",
doi = "10.1016/j.ceramint.2018.01.078",
url = "https://hdl.handle.net/21.15107/rcub_dais_4606"
}

Kosanović, D., Blagojević, V. A., Maričić, A., Aleksić, S., Pavlović, V. P., Pavlović, V. B.,& Vlahović, B.. (2018). Influence of mechanical activation on functional properties of barium hexaferrite ceramics. in Ceramics International
Elsevier., 44(6), 6666-6672.
https://doi.org/10.1016/j.ceramint.2018.01.078
https://hdl.handle.net/21.15107/rcub_dais_4606

Kosanović D, Blagojević VA, Maričić A, Aleksić S, Pavlović VP, Pavlović VB, Vlahović B. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. in Ceramics International. 2018;44(6):6666-6672.
doi:10.1016/j.ceramint.2018.01.078
https://hdl.handle.net/21.15107/rcub_dais_4606 .

Kosanović, Darko, Blagojević, Vladimir A., Maričić, Aleksa, Aleksić, S., Pavlović, Vera P., Pavlović, Vladimir B., Vlahović, Branislav, "Influence of mechanical activation on functional properties of barium hexaferrite ceramics" in Ceramics International, 44, no. 6 (2018):6666-6672,
https://doi.org/10.1016/j.ceramint.2018.01.078 .,
https://hdl.handle.net/21.15107/rcub_dais_4606 .

TY  - DATA
AU  - Kosanović, Darko
AU  - Blagojević, Vladimir A.
AU  - Maričić, Aleksa
AU  - Aleksić, S.
AU  - Pavlović, Vera P.
AU  - Pavlović, Vladimir B.
AU  - Vlahović, Branislav
PY  - 2018
UR  - https://ars.els-cdn.com/content/image/1-s2.0-S0272884218300919-mmc1.pdf
UR  - https://dais.sanu.ac.rs/123456789/3788
AB  - Rietveld analysis of XRD patterns of mechanically activated Fe:BaTiO3 powder mixtures sintered at 1200°C
T2  - Ceramics International
T1  - Kosanović, D., Blagojević, V.A., Maričić, A., Aleksić, S., Pavlović, V.P., Pavlović, V.B., Vlahović, B., 2018. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. Ceramics International 44, 6666–6672. https://doi.org/10.1016/j.ceramint.2018.01.078: Supplement
VL  - 44
IS  - 6
UR  - https://hdl.handle.net/21.15107/rcub_dais_3788
ER  - 

@misc{
author = "Kosanović, Darko and Blagojević, Vladimir A. and Maričić, Aleksa and Aleksić, S. and Pavlović, Vera P. and Pavlović, Vladimir B. and Vlahović, Branislav",
year = "2018",
abstract = "Rietveld analysis of XRD patterns of mechanically activated Fe:BaTiO3 powder mixtures sintered at 1200°C",
journal = "Ceramics International",
title = "Kosanović, D., Blagojević, V.A., Maričić, A., Aleksić, S., Pavlović, V.P., Pavlović, V.B., Vlahović, B., 2018. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. Ceramics International 44, 6666–6672. https://doi.org/10.1016/j.ceramint.2018.01.078: Supplement",
volume = "44",
number = "6",
url = "https://hdl.handle.net/21.15107/rcub_dais_3788"
}

Kosanović, D., Blagojević, V. A., Maričić, A., Aleksić, S., Pavlović, V. P., Pavlović, V. B.,& Vlahović, B.. (2018). Kosanović, D., Blagojević, V.A., Maričić, A., Aleksić, S., Pavlović, V.P., Pavlović, V.B., Vlahović, B., 2018. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. Ceramics International 44, 6666–6672. https://doi.org/10.1016/j.ceramint.2018.01.078: Supplement. in Ceramics International, 44(6).
https://hdl.handle.net/21.15107/rcub_dais_3788

Kosanović D, Blagojević VA, Maričić A, Aleksić S, Pavlović VP, Pavlović VB, Vlahović B. Kosanović, D., Blagojević, V.A., Maričić, A., Aleksić, S., Pavlović, V.P., Pavlović, V.B., Vlahović, B., 2018. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. Ceramics International 44, 6666–6672. https://doi.org/10.1016/j.ceramint.2018.01.078: Supplement. in Ceramics International. 2018;44(6).
https://hdl.handle.net/21.15107/rcub_dais_3788 .

Kosanović, Darko, Blagojević, Vladimir A., Maričić, Aleksa, Aleksić, S., Pavlović, Vera P., Pavlović, Vladimir B., Vlahović, Branislav, "Kosanović, D., Blagojević, V.A., Maričić, A., Aleksić, S., Pavlović, V.P., Pavlović, V.B., Vlahović, B., 2018. Influence of mechanical activation on functional properties of barium hexaferrite ceramics. Ceramics International 44, 6666–6672. https://doi.org/10.1016/j.ceramint.2018.01.078: Supplement" in Ceramics International, 44, no. 6 (2018),
https://hdl.handle.net/21.15107/rcub_dais_3788 .

TY  - JOUR
AU  - Aleksić, Obrad S.
AU  - Nikolić, Maria Vesna
AU  - Luković, Miloljub D.
AU  - Aleksić, S.
AU  - Nikolić, Pantelija M.
PY  - 2013
UR  - https://dais.sanu.ac.rs/123456789/340
AB  - A simple thermal sensor system was designed for measuring water flow in the water mains using the heat loss principle with a NTC thick film segmented thermistor as a self-heating sensor. Thick film segmented thermistors were screen printed on alumina substrate. NTC thermistor paste was formed of very fine Cu0.2Ni0.5Zn1.0Mn1.3O4 powder obtained by a combined mechanical activation/thermal treatment process, an organic vehicle and glass frit. The thermal sensor system was analyzed in the static and dynamic regime. A range constant voltage power supply was defined in the range 9–19 V for input water temperatures of 30–2 °C, maintaining a supply voltage in steps of 2 V for a change in 5 °C of input water temperature. This enables optimal operating power, i.e. heat generation on the self-heating thermistor. Measured calibration curves for different input water temperatures and input water flow rates were modeled, enabling interpolation of additional calculated curves to cover a wide range of input water temperatures.
PB  - Elsevier
T2  - Sensors and Actuators A: Physical
T1  - Analysis and optimization of a thermal sensor system for measuring water flow
SP  - 371
EP  - 376
VL  - 201
DO  - 10.1016/j.sna.2013.07.035
UR  - https://hdl.handle.net/21.15107/rcub_dais_340
ER  - 

@article{
author = "Aleksić, Obrad S. and Nikolić, Maria Vesna and Luković, Miloljub D. and Aleksić, S. and Nikolić, Pantelija M.",
year = "2013",
abstract = "A simple thermal sensor system was designed for measuring water flow in the water mains using the heat loss principle with a NTC thick film segmented thermistor as a self-heating sensor. Thick film segmented thermistors were screen printed on alumina substrate. NTC thermistor paste was formed of very fine Cu0.2Ni0.5Zn1.0Mn1.3O4 powder obtained by a combined mechanical activation/thermal treatment process, an organic vehicle and glass frit. The thermal sensor system was analyzed in the static and dynamic regime. A range constant voltage power supply was defined in the range 9–19 V for input water temperatures of 30–2 °C, maintaining a supply voltage in steps of 2 V for a change in 5 °C of input water temperature. This enables optimal operating power, i.e. heat generation on the self-heating thermistor. Measured calibration curves for different input water temperatures and input water flow rates were modeled, enabling interpolation of additional calculated curves to cover a wide range of input water temperatures.",
publisher = "Elsevier",
journal = "Sensors and Actuators A: Physical",
title = "Analysis and optimization of a thermal sensor system for measuring water flow",
pages = "371-376",
volume = "201",
doi = "10.1016/j.sna.2013.07.035",
url = "https://hdl.handle.net/21.15107/rcub_dais_340"
}

Aleksić, O. S., Nikolić, M. V., Luković, M. D., Aleksić, S.,& Nikolić, P. M.. (2013). Analysis and optimization of a thermal sensor system for measuring water flow. in Sensors and Actuators A: Physical
Elsevier., 201, 371-376.
https://doi.org/10.1016/j.sna.2013.07.035
https://hdl.handle.net/21.15107/rcub_dais_340

Aleksić OS, Nikolić MV, Luković MD, Aleksić S, Nikolić PM. Analysis and optimization of a thermal sensor system for measuring water flow. in Sensors and Actuators A: Physical. 2013;201:371-376.
doi:10.1016/j.sna.2013.07.035
https://hdl.handle.net/21.15107/rcub_dais_340 .

Aleksić, Obrad S., Nikolić, Maria Vesna, Luković, Miloljub D., Aleksić, S., Nikolić, Pantelija M., "Analysis and optimization of a thermal sensor system for measuring water flow" in Sensors and Actuators A: Physical, 201 (2013):371-376,
https://doi.org/10.1016/j.sna.2013.07.035 .,
https://hdl.handle.net/21.15107/rcub_dais_340 .