TY  - CONF
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Pavlović, Vladimir B.
AU  - Kosanović, Darko
AU  - Mitrić, Miodrag
AU  - Paunović, Vesna
AU  - Pouchly, V.
AU  - Kachlik, Martin
AU  - Maca, Karel
PY  - 2015
UR  - https://dais.sanu.ac.rs/123456789/763
AB  - Mechanically activated powders (0, 10, 40, 80 and 160 minutes) were formed by isostatic pressure 300 MPa to cylindrical green bodies (φ 12 mm). First set of samples was sintered at 1300°C for 30 min in air (heating rate 10 °C/min, cooling rate 5 oC/min). These samples were re-sintered at 1200 oC for 20 h in air (heating rate 20 °C/min, cooling rate 10 oC/min). Samples reached almost 90 % TD. The second set of samples was sintered at 1400 °C for 30 in air (heating rate 10 oC/min, cooling rate 5 °C/min). Relative densities increased up to 93 % TD. The samples of absence of open porosity (MTO-10, 40, 80 and 160) were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1200 °C for 2 h in argon atmosphere with pressure 200 MPa. The samples increased densities up to 96 % TD for sample MT-160. Electrical measurements were performed in the microwave field of frequency.
PB  - Belgrade : Serbian Ceramic Society
C3  - Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / IV Serbian Ceramic Society Conference, Belgrade, 21-23. September 2015
T1  - The effect of Hot Isostatic Pressing on the MT sample densities
SP  - 55
EP  - 55
UR  - https://hdl.handle.net/21.15107/rcub_dais_763
ER  - 

@conference{
author = "Filipović, Suzana and Obradović, Nina and Pavlović, Vladimir B. and Kosanović, Darko and Mitrić, Miodrag and Paunović, Vesna and Pouchly, V. and Kachlik, Martin and Maca, Karel",
year = "2015",
abstract = "Mechanically activated powders (0, 10, 40, 80 and 160 minutes) were formed by isostatic pressure 300 MPa to cylindrical green bodies (φ 12 mm). First set of samples was sintered at 1300°C for 30 min in air (heating rate 10 °C/min, cooling rate 5 oC/min). These samples were re-sintered at 1200 oC for 20 h in air (heating rate 20 °C/min, cooling rate 10 oC/min). Samples reached almost 90 % TD. The second set of samples was sintered at 1400 °C for 30 in air (heating rate 10 oC/min, cooling rate 5 °C/min). Relative densities increased up to 93 % TD. The samples of absence of open porosity (MTO-10, 40, 80 and 160) were post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1200 °C for 2 h in argon atmosphere with pressure 200 MPa. The samples increased densities up to 96 % TD for sample MT-160. Electrical measurements were performed in the microwave field of frequency.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / IV Serbian Ceramic Society Conference, Belgrade, 21-23. September 2015",
title = "The effect of Hot Isostatic Pressing on the MT sample densities",
pages = "55-55",
url = "https://hdl.handle.net/21.15107/rcub_dais_763"
}

Filipović, S., Obradović, N., Pavlović, V. B., Kosanović, D., Mitrić, M., Paunović, V., Pouchly, V., Kachlik, M.,& Maca, K.. (2015). The effect of Hot Isostatic Pressing on the MT sample densities. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / IV Serbian Ceramic Society Conference, Belgrade, 21-23. September 2015
Belgrade : Serbian Ceramic Society., 55-55.
https://hdl.handle.net/21.15107/rcub_dais_763

Filipović S, Obradović N, Pavlović VB, Kosanović D, Mitrić M, Paunović V, Pouchly V, Kachlik M, Maca K. The effect of Hot Isostatic Pressing on the MT sample densities. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / IV Serbian Ceramic Society Conference, Belgrade, 21-23. September 2015. 2015;:55-55.
https://hdl.handle.net/21.15107/rcub_dais_763 .

Filipović, Suzana, Obradović, Nina, Pavlović, Vladimir B., Kosanović, Darko, Mitrić, Miodrag, Paunović, Vesna, Pouchly, V., Kachlik, Martin, Maca, Karel, "The effect of Hot Isostatic Pressing on the MT sample densities" in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / IV Serbian Ceramic Society Conference, Belgrade, 21-23. September 2015 (2015):55-55,
https://hdl.handle.net/21.15107/rcub_dais_763 .

TY  - CONF
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Pavlović, Vladimir B.
AU  - Kosanović, Darko
AU  - Mitrić, Miodrag
AU  - Paunović, Vesna
AU  - Pouchly, V.
AU  - Kachlik, Martin
AU  - Maca, Karel
PY  - 2014
UR  - https://dais.sanu.ac.rs/123456789/638
AB  - Poster presented at the III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014
T1  - Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering
UR  - https://hdl.handle.net/21.15107/rcub_dais_638
ER  - 

@conference{
author = "Filipović, Suzana and Obradović, Nina and Pavlović, Vladimir B. and Kosanović, Darko and Mitrić, Miodrag and Paunović, Vesna and Pouchly, V. and Kachlik, Martin and Maca, Karel",
year = "2014",
abstract = "Poster presented at the III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014",
title = "Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering",
url = "https://hdl.handle.net/21.15107/rcub_dais_638"
}

Filipović, S., Obradović, N., Pavlović, V. B., Kosanović, D., Mitrić, M., Paunović, V., Pouchly, V., Kachlik, M.,& Maca, K.. (2014). Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering. .
https://hdl.handle.net/21.15107/rcub_dais_638

Filipović S, Obradović N, Pavlović VB, Kosanović D, Mitrić M, Paunović V, Pouchly V, Kachlik M, Maca K. Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering. 2014;.
https://hdl.handle.net/21.15107/rcub_dais_638 .

Filipović, Suzana, Obradović, Nina, Pavlović, Vladimir B., Kosanović, Darko, Mitrić, Miodrag, Paunović, Vesna, Pouchly, V., Kachlik, Martin, Maca, Karel, "Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering" (2014),
https://hdl.handle.net/21.15107/rcub_dais_638 .

TY  - CONF
AU  - Filipović, Suzana
AU  - Obradović, Nina
AU  - Pavlović, Vladimir B.
AU  - Kosanović, Darko
AU  - Mitrić, Miodrag
AU  - Paunović, Vesna
AU  - Pouchly, V.
AU  - Kachlik, Martin
AU  - Maca, Karel
PY  - 2014
UR  - https://dais.sanu.ac.rs/123456789/614
AB  - The aim of this paper was investigation of structural and electrical properties of magnesium titanate ceramic obtained mechanochemically and subjected to two stage sintering process. Mixtures of MgO and TiO2 were treated in a planetary ball mill for several time intervals ranging from 0 to 160 minutes. Powders prepared in this way were two stage sintered, at 1400 °C in air in the first stage, and then post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1280 °C in argon atmosphere with a pressure of 200 MPa. X-ray diffraction was performed in order to established phase composition of obtained ceramics. Densities of sintered samples were measured by Archimedes method. The values of density were over 96 % of theoretical one and pure MgTiO3 phase was observed. Morphology of sintered bodies was investigated by SEM, and micrographs indicate the final sintering stage and very dense ceramics. Electrical measurements were performed in the microwave field of frequency.
PB  - Belgrade : Serbian Ceramic Society
C3  - Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014
T1  - Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering
SP  - 118
EP  - 118
UR  - https://hdl.handle.net/21.15107/rcub_dais_614
ER  - 

@conference{
author = "Filipović, Suzana and Obradović, Nina and Pavlović, Vladimir B. and Kosanović, Darko and Mitrić, Miodrag and Paunović, Vesna and Pouchly, V. and Kachlik, Martin and Maca, Karel",
year = "2014",
abstract = "The aim of this paper was investigation of structural and electrical properties of magnesium titanate ceramic obtained mechanochemically and subjected to two stage sintering process. Mixtures of MgO and TiO2 were treated in a planetary ball mill for several time intervals ranging from 0 to 160 minutes. Powders prepared in this way were two stage sintered, at 1400 °C in air in the first stage, and then post-sintered by pressure assisted technique Hot Isostatic Pressing (HIP) at 1280 °C in argon atmosphere with a pressure of 200 MPa. X-ray diffraction was performed in order to established phase composition of obtained ceramics. Densities of sintered samples were measured by Archimedes method. The values of density were over 96 % of theoretical one and pure MgTiO3 phase was observed. Morphology of sintered bodies was investigated by SEM, and micrographs indicate the final sintering stage and very dense ceramics. Electrical measurements were performed in the microwave field of frequency.",
publisher = "Belgrade : Serbian Ceramic Society",
journal = "Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014",
title = "Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering",
pages = "118-118",
url = "https://hdl.handle.net/21.15107/rcub_dais_614"
}

Filipović, S., Obradović, N., Pavlović, V. B., Kosanović, D., Mitrić, M., Paunović, V., Pouchly, V., Kachlik, M.,& Maca, K.. (2014). Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014
Belgrade : Serbian Ceramic Society., 118-118.
https://hdl.handle.net/21.15107/rcub_dais_614

Filipović S, Obradović N, Pavlović VB, Kosanović D, Mitrić M, Paunović V, Pouchly V, Kachlik M, Maca K. Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering. in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014. 2014;:118-118.
https://hdl.handle.net/21.15107/rcub_dais_614 .

Filipović, Suzana, Obradović, Nina, Pavlović, Vladimir B., Kosanović, Darko, Mitrić, Miodrag, Paunović, Vesna, Pouchly, V., Kachlik, Martin, Maca, Karel, "Properties of Magnesium Titanate Ceramic Obtained by Two Stage Sintering" in Advanced Ceramics and Application : new frontiers in multifunctional material science and processing : program and the book of abstracts / III Serbian Ceramic Society Conference, 29th September - 1st October, Belgrade, 2014 (2014):118-118,
https://hdl.handle.net/21.15107/rcub_dais_614 .