TY  - JOUR
AU  - Labus, Nebojsa
AU  - Krstić, Jugoslav
AU  - Matijašević, Srđan
AU  - Pavlović, Vladimir
PY  - 2023
UR  - https://dais.sanu.ac.rs/123456789/15141
AB  - Powder mixture consisted of ZnO, Mn2O3 (MnCO3) and Fe2O3 blended powders, was found laminating during compaction. Polyvinyl alcohol (PVA) and a combination of PVA with polyethylene glycol (PEG) added as a plasticizer, were introduced as polymer binders to improve the compaction of oxide mixtures. It has been done by forming a suspension of oxide mixture and varying the polymer solution concentration and composition. By evaporating the solvent, new materials were obtained, which consist of oxide particles bound via polymer. In such a manner obtained hybrid materials were characterized with attenuated total reflection Fourier transformed infrared (ATR-FTIR) spectroscopy, differential thermal analysis (DTA) and transmission electron microscopy (TEM). The oxide polymer material was compacted at 200 MPa and the expansion of this compact during heating was monitored in temperature range up to 550ºC with dilatometer. It was found that PVA forms graft polymer with PEG and specific interaction with oxide particles surface was revealed.
AB  - Смеша прахова састављена од ZnO, Mn2O3 (MnCO3) и Fe2O3 комбинацијепрахова је показивала ламинацију током пресовања. Поливинил алкохол (PVA) икомбинација PVA са полиетилен гликолом (PEG) који је додат као пластификатор, сууведени као полимерно везиво за пресовање оксидних прахова. Везиво је уведено такошто је формирана суспензија смеше различитих оксида прахова у полимерномраствору. Концентрације полимера и састави су варирани. Уклањањем растварачадобијени су нови материјали који се састоје од честица оксида повезаних полимерима.Ови хибридни материјали окарактерисани су методама ометене тоталне рефлексијефурије трансформисане инфрацрвене спектроскопије (ATR-FTIR) као идиференцијалне термичке анализе (DTA). Микроструктура је посматранатрансмисоном електронском микроскопијом (TEM). Оксид-полимер материјали супресовани на притиску од 200 MPa и ширење испреска током грејања је праћено у температурском опсегу од собне до 550ºC употребом дилатометра. Нађено је да PVAформира графт полимер са PEG и да постоји специфична интеракција полимера саповршином честица оксида.
PB  - Belgrade : Association for ETRAN Society
T2  - Science of Sintering
T1  - Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer
SP  - 189
EP  - 2023
VL  - 55
DO  - 10.2298/SOS220828005L
UR  - https://hdl.handle.net/21.15107/rcub_dais_15141
ER  - 

@article{
author = "Labus, Nebojsa and Krstić, Jugoslav and Matijašević, Srđan and Pavlović, Vladimir",
year = "2023",
abstract = "Powder mixture consisted of ZnO, Mn2O3 (MnCO3) and Fe2O3 blended powders, was found laminating during compaction. Polyvinyl alcohol (PVA) and a combination of PVA with polyethylene glycol (PEG) added as a plasticizer, were introduced as polymer binders to improve the compaction of oxide mixtures. It has been done by forming a suspension of oxide mixture and varying the polymer solution concentration and composition. By evaporating the solvent, new materials were obtained, which consist of oxide particles bound via polymer. In such a manner obtained hybrid materials were characterized with attenuated total reflection Fourier transformed infrared (ATR-FTIR) spectroscopy, differential thermal analysis (DTA) and transmission electron microscopy (TEM). The oxide polymer material was compacted at 200 MPa and the expansion of this compact during heating was monitored in temperature range up to 550ºC with dilatometer. It was found that PVA forms graft polymer with PEG and specific interaction with oxide particles surface was revealed., Смеша прахова састављена од ZnO, Mn2O3 (MnCO3) и Fe2O3 комбинацијепрахова је показивала ламинацију током пресовања. Поливинил алкохол (PVA) икомбинација PVA са полиетилен гликолом (PEG) који је додат као пластификатор, сууведени као полимерно везиво за пресовање оксидних прахова. Везиво је уведено такошто је формирана суспензија смеше различитих оксида прахова у полимерномраствору. Концентрације полимера и састави су варирани. Уклањањем растварачадобијени су нови материјали који се састоје од честица оксида повезаних полимерима.Ови хибридни материјали окарактерисани су методама ометене тоталне рефлексијефурије трансформисане инфрацрвене спектроскопије (ATR-FTIR) као идиференцијалне термичке анализе (DTA). Микроструктура је посматранатрансмисоном електронском микроскопијом (TEM). Оксид-полимер материјали супресовани на притиску од 200 MPa и ширење испреска током грејања је праћено у температурском опсегу од собне до 550ºC употребом дилатометра. Нађено је да PVAформира графт полимер са PEG и да постоји специфична интеракција полимера саповршином честица оксида.",
publisher = "Belgrade : Association for ETRAN Society",
journal = "Science of Sintering",
title = "Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer",
pages = "189-2023",
volume = "55",
doi = "10.2298/SOS220828005L",
url = "https://hdl.handle.net/21.15107/rcub_dais_15141"
}

Labus, N., Krstić, J., Matijašević, S.,& Pavlović, V.. (2023). Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer. in Science of Sintering
Belgrade : Association for ETRAN Society., 55, 189-2023.
https://doi.org/10.2298/SOS220828005L
https://hdl.handle.net/21.15107/rcub_dais_15141

Labus N, Krstić J, Matijašević S, Pavlović V. Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer. in Science of Sintering. 2023;55:189-2023.
doi:10.2298/SOS220828005L
https://hdl.handle.net/21.15107/rcub_dais_15141 .

Labus, Nebojsa, Krstić, Jugoslav, Matijašević, Srđan, Pavlović, Vladimir, "Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer" in Science of Sintering, 55 (2023):189-2023,
https://doi.org/10.2298/SOS220828005L .,
https://hdl.handle.net/21.15107/rcub_dais_15141 .