@article{
author = "Zdujić, Miodrag and Poleti, Dejan and Jovalekić, Čedomir and Karanović, Ljiljana",
year = "2009",
abstract = "A powder mixture of α-Bi2O3 and HfO2, in the molar ratio 2:3, was mechanochemically treated in a planetary ball mill under air, using zirconium oxide vials and balls as the milling medium. After 50 h of milling, the mechanochemical reaction led to the formation of a nanocrystalline δ-Bi2O3 phase (fluorite-type solid solution Bi0.78Hf0.59Zr0.63O3.61), with a crystallite size of 20 nm. The mechanochemical reaction started at a very beginning of milling accompanied by an accumulation of ZrO2 arising from the milling tools. The samples prepared after various milling times were characterized by X-ray powder diffraction and DSC analysis. The electrical properties of the as-milled and pressed Bi0.78Hf0.59Zr0.63O3.61 powder were studied using impedance spectroscopy in the temperature range from 100 to 700°C under air. The electrical conductivity was determined to be 9.43×10-6 and 0.080 S cm-1 for the temperatures of 300 and 700°C, respectively., Smeša prahova α-Bi2O3 i HfO2 u molarnom odnosu 2:3 mehanohemijski je tretirana u planetarnom mlinu u atmosferi vazduha, koristeći cirkonijumske posude i kuglice kao medijum za mlevenje. Posle 50 h mlevenja, mehanohemijska reakcija dovodi do stvaranja nanokristalne δ-Bi2O3 faze (čvrsti rastvor fluoritske strukture Bi0,78Hf0,59Zr0,63O3,61), veličine kristalita 20 nm. Mehanohemijska reakcija otpočinje u samom početku mlevenja i praćena je akumulacijum ZrO2 koji potiče od medijuma za mlevenje. Uzorci dobijeni posle različitih vremena mlevenja karakterisani su rendgenskom strukturnom i termijskom analizom. Električna svojstva mlevenih i presovanih Bi0,78Hf0,59Zr0,63O3,61 prahova ispitivana su impedansnom spektroskopijom u temperaturnom opsegu od 100 do 700°C. Dobijena električna provodnost je 9,43·10-6 i 0,080 S cm-1 za temperaturu 300 i 700°C, redom.",
publisher = "Belgrade : Serbian Chemical Society",
journal = "Journal of the Serbian Chemical Society",
title = "Mechanochemical synthesis and electrical conductivity of nanocrystalline δ-Bi2O3 stabilized by HfO2 and ZrO2",
pages = "1401-1411",
volume = "74",
number = "12",
doi = "10.2298/JSC0912401Z",
url = "https://hdl.handle.net/21.15107/rcub_dais_174"
}