Physical Properties of Sintered Alumina Doped with Different Oxides
Аутори
Filipović, SuzanaObradović, Nina
Marković, Smilja
Đorđević, Antonije
Balać, Igor
Dapčević, Aleksandra
Rogan, Jelena
Pavlović, Vladimir B.
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
Corundum (α-alumina) is a suitable material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 oC and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm3. Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for ...the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.
Кључне речи:
mechanical activation / alumina / sintering / SEMИзвор:
Science of Sintering, 2018, 50, 4, 409-419Издавач:
- Belgrade : ETRAN
Финансирање / пројекти:
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-MESTD-Basic Research (BR or ON)-172057)
- 0-3D наноструктуре за примену у електроници и обновљивим изворима енергије: синтеза, карактеризација и процесирање (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45007)
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45019)
DOI: 10.2298/SOS1804409F
ISSN: 1820-7413
WoS: 000455876800003
Scopus: 2-s2.0-85062894934
Институција/група
Институт техничких наука САНУ / Institute of Technical Sciences of SASATY - JOUR AU - Filipović, Suzana AU - Obradović, Nina AU - Marković, Smilja AU - Đorđević, Antonije AU - Balać, Igor AU - Dapčević, Aleksandra AU - Rogan, Jelena AU - Pavlović, Vladimir B. PY - 2018 UR - https://dais.sanu.ac.rs/123456789/4537 AB - Corundum (α-alumina) is a suitable material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 oC and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm3. Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures. PB - Belgrade : ETRAN T2 - Science of Sintering T1 - Physical Properties of Sintered Alumina Doped with Different Oxides SP - 409 EP - 419 VL - 50 IS - 4 DO - 10.2298/SOS1804409F UR - https://hdl.handle.net/21.15107/rcub_dais_4537 ER -
@article{ author = "Filipović, Suzana and Obradović, Nina and Marković, Smilja and Đorđević, Antonije and Balać, Igor and Dapčević, Aleksandra and Rogan, Jelena and Pavlović, Vladimir B.", year = "2018", abstract = "Corundum (α-alumina) is a suitable material for usage in various industry fields owing to its chemical stability, electrical and mechanical features. It is known that properties of ceramics could be modified by addition of different oxides, as well as by changing the consolidation parameters. In this respect, alumina was doped with 1 wt.% of Cr2O3, Mn2O3 and NiO, followed by 1 hour of mechanical activation in a high-energy planetary ball mill. A sensitive dilatometer was used for sintering of powder mixtures up to 1400 oC and recording the obtained dilatation. The final density varied between cca. 1.9 and 3.3 g/cm3. Microstructural changes were detected by SEM measurements. Changes in electrical permittivity and loss tangent were associated with the preparation conditions (types of additives, duration of mechanical activation). For a given mixture, the sintering increases the relative permittivity and decreases losses, exhibiting the optimal values of 8.32 and 0.027, respectively, for the sample activated 60 minutes and sintered, with the addition of MnO2. Mechanical measurements indicate significant differences in strength with the addition of different transition metal oxides. Samples with Mn and Ni, activated and sintered, with strength of 121 and 86 MPa, respectively, have a significantly higher tensile strength than the other tested samples, due to their more compact microstructures.", publisher = "Belgrade : ETRAN", journal = "Science of Sintering", title = "Physical Properties of Sintered Alumina Doped with Different Oxides", pages = "409-419", volume = "50", number = "4", doi = "10.2298/SOS1804409F", url = "https://hdl.handle.net/21.15107/rcub_dais_4537" }
Filipović, S., Obradović, N., Marković, S., Đorđević, A., Balać, I., Dapčević, A., Rogan, J.,& Pavlović, V. B.. (2018). Physical Properties of Sintered Alumina Doped with Different Oxides. in Science of Sintering Belgrade : ETRAN., 50(4), 409-419. https://doi.org/10.2298/SOS1804409F https://hdl.handle.net/21.15107/rcub_dais_4537
Filipović S, Obradović N, Marković S, Đorđević A, Balać I, Dapčević A, Rogan J, Pavlović VB. Physical Properties of Sintered Alumina Doped with Different Oxides. in Science of Sintering. 2018;50(4):409-419. doi:10.2298/SOS1804409F https://hdl.handle.net/21.15107/rcub_dais_4537 .
Filipović, Suzana, Obradović, Nina, Marković, Smilja, Đorđević, Antonije, Balać, Igor, Dapčević, Aleksandra, Rogan, Jelena, Pavlović, Vladimir B., "Physical Properties of Sintered Alumina Doped with Different Oxides" in Science of Sintering, 50, no. 4 (2018):409-419, https://doi.org/10.2298/SOS1804409F ., https://hdl.handle.net/21.15107/rcub_dais_4537 .