Title: Photocatalysis data of β NaY0.78F4:Yb0.2Tm0.02; System 1 EDTA, Experiment 1, SamplesHex,Hex@TiO2Acac & Hex@TiO2Acac 300

Abstract: Photocatalysisdata of β NaY0.78F4:Yb0.2Tm0.02 were performed with irradiation source comprised DULUXD/E 26 W residential fluorescent lamp with an irradiance of 0.23 W cm..2 (400–700 nm) and NIR LED diode SMB1N-980D of 400 mW (RoithnerLaserTechnik, Wien, Austria).Thetetracycline degradation tests were performed under vigorous magnetic stirring, using200 mg L-1 of the core-shell material. Comparative photocatalytic tests were completed sing 25 mg L-1 of TiO2-Acac nanoparticles, since this amount corresponds to the theoretical mass of the 50 nm-thick TiO2-Acac shell. After ensuring the adsorption–desorption equilibrium in darkness (1 h) the lamps were turned on, and 5 mL aliquots of supernatant were acquired at designed time intervals. The supernatant was double-filtered, using a Merck Millipore filter (0.45 µm), and analyzed by a UV-Vis spectrophotometer (Agilent8453, Santa Clara, CA, USA), for CORE-SHELL Project, samples were synthesized through EDTA assisted solvothermal processing, Et:H2O=2:1, FF=60 %, c=0.01 M, 200°C/2h; Re:NaF=1:14, Re:EDTA=1:1, and coated withTiO2-Acac.Data were collected on 11/11/22

***Column headers and field types*** 
Time, min (number.decimal); 
C/C (number.decimal)

***Dataset contents***
TC_degradation_Hex.tif (120.8Mb)
TC_degradation-Hex_TiO2-Acac.tif (120.8Mb)
TC_degradation-Hex TiO2-Acac_300.tif (120.8Mb)
TC_degradation-TiO2-Acac-300-25mg.tif (120.8Mb)
Photocatalysis-Samples_Hex1_TiO2acac-and_Hex1_TiO2acac_300_final.tif (120.8Mb)
README.txt

Handle: https://hdl.handle.net/21.15107/rcub_dais_14752