The Influence of Synthesis Parameters and Heat Effect on Magnetic Properties of Powder System FexOy - BaTiO3
(Belgrade : Serbian Ceramic Society, 2015)
Powder mixture of 60 mass % of iron (Fe) and 40 mass % of barium titanate (BaTiO3) has been activated in planetary mill for 100, 120, 150, 180, 210 and 240 min in the air. During the activation the iron powder transits ...
The effect of Hot Isostatic Pressing on the MT sample densities
(Belgrade : Serbian Ceramic Society, 2015)
Mechanically activated powders (0, 10, 40, 80 and 160 minutes) were formed by isostatic pressure 300 MPa to cylindrical green bodies (φ 12 mm). First set of samples was sintered at 1300°C for 30 min in air (heating rate ...
Structural investigation of mechanically activated ZnO powder
(Elsevier, 2015)
Abstract Commercially available ZnO powder was mechanically activated in a planetary ball mill. In order to investigate the specific surface area, pore volume and microstructure of non-activated and mechanically activated ...
Uticaj mehaničke aktivacije na svojstva MgO-TiO2 elektrokeramike
(Čačak : University of Kragujevac, Faculty of Technical Sciences, 2015)
Intenzivan razvoj elektronike najvećim delom zavisi od razvoja novih materijala, koji se pored strogo određenog sastava odlikuju i tačno određenom raspodelom defekata i primesa. Sa sve rasprostranjenijom primenom tehnike ...
Investigation of thermally induced processes in corundum refractory concretes with addition of fly ash
(Springer Netherlands, 2015)
The effects that the fly ash addition has on the behavior of thermally resistant corundum concrete were discussed. Experimental program implied production of two refractory composites: "referent" concrete from 20 % of ...
Microstructure development and Raman responses of mechanically activated Fe/BaTiO3
(Belgrade : Serbian Ceramic Society, 2015)
The structure and lattice dynamics of mechanically activated nanocrystalline Fe/BaTiO3 is investigated in this work. The powder mixture of 60%Fe and 40% BaTiO3 was mechanically activated up to 240 min in 500 cm3 zirconium ...
Reaction kinetics of mechanically activated cordierite based ceramics studied via DTA
(Ljubljana : Central and Eastern European Committee for Thermal Analysis and Calorimetry, 2015)
Cordierite, 2MgO•2Ah03•5Si02 (MAS), is a very attractive high-temperature ceramic material. In order to accelerate the process of sintering, 5.00 mass% Mo03 was added to the starting mixtures. The mechanical activation of ...
The influence of compaction pressure on the density and electrical properties of cordierite-based ceramics
(Belgrade : International Institute for the Science of Sintering, 2015)
Due to its characteristics, cordierite, 2MgO·2Al2O3·5SiO2, is a high-temperature ceramic material of a great scientific interest. Mechanical activation of the starting mixtures containing 5.00 mass% TiO2 was performed in ...