Influence of nitrogen and air atmosphere during thermal treatment on micro and nano sized powders and sintered TiO2 specimens
(Belgrade : International Institute for the Science of Sintering, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment
(Science of Sintering, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Reheating of zinc-titanate sintered specimens
(Belgrade : International Institute for the Science of Sintering, 2015)
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during heating in nitrogen and air atmosphere. Interactions of bulk specimens with gaseous surrounding induce microstructure ...
Analysis of the initial-stage sintering of mechanically activated SrTiO3
(ETRAN, 2019)
The initial-stage of sintering plays a significant role in determining the final microstructure that defines the main characteristics of electroceramics materials such as functional properties. In this article non-isothermal ...
Influence of nitrogen and air atmosphere during thermal treatment on micro and nano sized powders and sintered TiO2 specimens
(Science of Sintering, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...