Structural, electrical and magnetic properties of mechanically activated manganese and zinc ferrite
(Belgrade : Institute for Multidisciplinary Research of the University of Belgrade, 2017)
Starting hematite (Fe2O3), zinc oxide (ZnO) and manganese carbonate (MnCO3) powders were homogenized in a planetary ball mill in stainless steel bowls with stainless steel balls for 15 min, calcined in air at 1000 C for ...
Influence of synthesis parameters and thermal treatment on functional properties of Fe3O4-BaTiO3 multiferroics obtained by mechanical activation
(Belgrade : Serbian Ceramic Society, 2017)
Mechanical activation of a mixture of polycrystalline powders Fe3O4 (50% wt.) and BaTiO3 (50% wt.) was performed in a planetary ball-mill, with different milling times (3 h, 6 h and 12 h). Average crystallite size determined ...
Synthesis of BaFe12O19-BaTiO3 multiferroics by mechanical activation
(Belgrade : Serbian Ceramic Society, 2017)
A mixture of polycrystalline powders of Fe (70 % wt.) and BaTiO3 (30 % wt.) was ball-milled in a planetary mill under air atmosphere, for different time intervals: 60, 120, 180, 240, 300 and 360 min. During the mechanical ...
Microwave Electro Ceramic Based on Magnesium Titanate Compounds
(Paris : Atlantis Press, 2017)
The intensive progress in electronics, especially telecommunication and mobile phone in 1990s, was the main driving force for the extensive research and development of microwave ceramics. These materials are often used in ...
Synthesis and Characterization of Multifferoics 16%(Fe2O3)4%(BaCO3)80%(BaTiO3)
(Belgrade : Serbian Ceramic Society, 2017)
The initial powder (16 % Fe2O3, 4 % BaCO3, 80 % BaTiO3) was mechanically activated in a planetary mill for 20, 80, 120, 160, 200 and 220 minutes in air. Modified Faraday method was used to perform magnetization measurements ...